Abstract:Arrays of randomly oriented zinc oxide (ZnO) nanowires were fabricated on silicon wafers via a simple thermal evaporation method. During the fabrication, the temperature around the substrate was below 500°C. The products were analyzed by conventional means and determined to be single crystals of wurtzite-type ZnO that grew along the c-axis. These nanowires were 10–100nm in diameter and 10–100μm in length, suggesting a possible high field enhancement factor. The dependence of the field emission current on the anode–cathode voltage (I–V behavior) of the ZnO nanowire arrays was measured in a lab-built ultrahigh vacuum system with a base pressure of 10−7Pa. After surface cleaning by heat treatment, two characteristic electric fields, under which 10μA/cm2 and 1mA/cm2 current densities were extracted, were measured to be 4.0 and 4.7V/μm, respectively. As observed with a transparent anode, emission occurred uniformly over the whole sample surface. A 72h-long test on emission stability was performed under a constant voltage of 2.75kV. The current dropped occasionally to approximately 80% of the initial value during the test owing to the poor adherence of the nanowires to the substrate. These preliminary results have shown the perspective of, as well as a major drawback to, a ZnO nanowire array being developed into a cold electron source to be used in future electronic devices.

Influence of Annealing on Field Emission Properties of Zinc Oxide Nanowires

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Enhanced Visible Light Response of ZnO Porous Thin Film by Post-Annealing Treatment

Field Emission Microscopy Study of Zinc Oxide Nanowires on Tungsten Tip

Annealing-Induced Change of Hydrogen Behavior in Zno Nanorods Revealed by Photoluminescence

Enhanced Field Emission from Zno Nanorods Via Thermal Annealing in Oxygen

Field Emission from Zinc Oxide Nanostructures and Its Degradation

Field Emission Properties of Zinc Oxide Nanowires Fabricated by Thermal Evaporation

Influence of Annealing on Field Emission Characteristics of Single-walled Carbon Nanotubes Assembled on Tungsten Tip

Annealing Effects on the Microstructure and Photoluminescence Properties of Ni-Doped Zno Films

Field Emission from Nonaligned Zinc Oxide Nanowires

Microstructure Change of ZnO Nanowire Induced by Energetic X-Ray Radiation and Its Effect on the Field Emission Properties

Amazing Ageing Property and in Situ Comparative Study of Field Emission from Tungsten Oxide Nanowires

Field Emission Properties of ZnO Nanowire Array Directly Grown from Zinc Substrate

Effects of Annealing on the Ferromagnetism and Photoluminescence of Cu-Doped Zno Nanowires

Influence of Postdeposition Annealing on Crystallinity of Zinc Oxide Films

Annealing-induced changes of the 3.31 eV emission in ZnO nanorods

Stable, Self-Ballasting Field Emission from Zinc Oxide Nanowires Grown on an Array of Vertically Aligned Carbon Nanofibers

Photosensitivity Effect of Field Emission from Zinc Oxide Nanowires

Fabrication of ZnO Nanowires by Vapor-Phase Deposition and Their Field Emission Properties

Annealing Effects On The Field Emission Properties Of Aln Nanorods