Effect of annealing on the magnetic properties of solution synthesized Zn1-xMnxO nanorods
HanBin Wang,Hao Wang,Cong Zhang,Fujun Yang,Chun Yang,Haoshuang Gu,Minjie Zhou,Quan Li,Yong Jiang
DOI: https://doi.org/10.1016/j.matchemphys.2008.08.063
IF: 4.778
2009-01-01
Materials Chemistry and Physics
Abstract:Mn-doped ZnO nanorods with ∼30nm in diameter and ∼200nm in length were synthesized by a seed-mediated solution method. The structures, magnetic properties, as well as the annealing effect were characterized by transmission electron microscopy, electron energy loss spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectrum and physical properties measurement system. Magnetic properties measurement revealed that the Zn0.97Mn0.03O nanorods exhibited ferromagnetism with a saturation magnetization of 0.005emug−1 and a coercivity of 110Oe at 305K. After annealing the samples at 900°C for 2h in air, the nanorods were transformed into nanoparticle aggregates. The coercivity and saturation magnetization increased obviously. Detailed analyses proved that a phase-separation process was happened at the high temperature. In this process, most of the particles preserved the wurtzite ZnO structure, while a few small ones evolved into spinel-structured particles. The increasing of the ferromagnetism of the annealed sample is attributed to the formation of secondary phase ZnxMn3−xO4.