Abstract:Nanosized copper oxide-zirconia particles containing 10-30 mol% of copper were prepared by using a precipitation technique in aqueous tetramethylammonium hydroxide solutions. Two methods, in situ (INS) and step-by-step (SBS), which differed in the time when the copper salt was introduced to the synthesis procedure, were used, and this allowed a comparison of the properties of the final powders produced using the two modes of preparation. The surface areas and phase compositions were different for the samples prepared from the two different methods after calcination at 500 degreesC. A surface area of 168 m(2) g(-1) was obtained for the sample prepared with the SBS method and 121 m(2) g(-1) for the INS method, both contain 30 mol% copper. Tetragonal ZrO2 was observed from X-ray diffraction patterns for all samples prepared with the SBS method, however, no separate phase of copper or copper oxide was observed. It is proposed that all of the copper is finely distributed on the surface of the ZrO2 particles with the SBS method. For the samples prepared from the INS method, tetragonal ZrO2 was obtained at a low copper content and the peaks indexed to tetragonal ZrO2 shifted to higher angle with the increase of copper content, indicating copper ions being incorporated into the lattice. An amorphous compound was obtained at high copper content (30 mol%). The phase change with the calcination temperature was also investigated for the INS sample containing 30 mol% copper. The studies show that tetragonal ZrO2 and copper oxide were present after calcination at 400 degreesC, and tetragonal ZrO2 with a small amount of monoclinic ZrO2, as well as copper oxide, formed after calcination at 700 degreesC. However, after heating at 500 degreesC, amorphous compounds were obtained, suggesting that 500 degreesC could be a phase transition point. The incorporation of copper in the ZrO2 lattice resulted in a loss of order in the ZrO2 structure when calcined at 500 degreesC, with a further increase in the calcination temperature leading to the phase change.

Preparation and Characterization of Crox/Zro2 with High Thermal Stability and High Specific Surface Area

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation of High-Surface-Area Sno2 and Zro2 by Reflux-Digestion and Solvothermal Methods

Preparation and Characterization of Zirconium Carbide Nano Powder by Hydrothermal and Carbothermal Reduction Methods

Preparation of High Surface Area Zirconia by RefluxDigestion in Basic Solutions

Preparation and characterization of high specific surface area Ce 0.5Zr0.5O2 mixed oxide

Mesoporous Yttria-Zirconia Solid Solution with Improved Textural Properties Prepared Via Lauric Acid-Assisted Synthesis

Effect of Preparation Method on Surface Area and Crystalline Form of Ceo2-Zro2 Solid Solution

The Effect of the Preparation Methods on the Structure of Wo3/Zro7

Preparation of SiO2 modified SnO2 and ZrO2 with novel thermal stability

Preparation and characterization of nano-scale Y2O3-ZrO2 powder by heterogeneous precipitation

Preparation and Characterization of Mesoporous Tetragonal Sulfated Zirconia

Preparation of Ceria-Zirconia Solid Solution by Urea-Based Hydrothermal-Copricipitation Method and its Catalytic Application

Synthesis and Characterization of Thermally Stable Mesostructured Sulfated Zirconia by a Novel Sulfate-Assisted Alcohothermal Route

Preparations and Characterizations of New Mesoporous ZrO2 and Y2O3-stabilized ZrO2 Spherical Powders

Preparation and characterization of metal oxide supported silica pillared zirconium phosphates with high surface area

Preparation and Characterization of Mesoporous Zirconia Materials by Self-Assembly Method

Effects of Zr on the Precursor Architecture and High-Temperature Nanostructure Evolution of Sioc Polymer-Derived Ceramics

Effect of Preparation Method on the Surface and Redox Properties of Ce0.67zr0.33o2 Mixed Oxides

Preparation and characterization of CuO–ZrO2 nanopowders

Preparation and Thermal Stability of Zirconia-Doped Mullite Fibers Via Sol-Gel Method