Abstract:alpha-FeOOH nanocrystals were synthesized in high yield via a facile and template-free hydrothermal method at low temperature. The morphology and composition of the samples were controlled by slowly releasing the SO42- ions from ammonium persulfate. The rod-like, bundle-like, and urchin-like alpha-FeOOH nanocrystals could be acquired respectively through a direct hydrothermal route with different quantities of SO42- ions. The rod-like a-FeOOH nanocrystals obtained have a diameter of 5-25 nm and a length of 100-200 nm. When the molar ratio of iron to SO42- was 1:1, the product was pure a-FeOOH phase. However, as the molar ratio was decreased from 1:1 to 1:4, pure FeSO4OH center dot 2H(2)O phase was obtained. When the molar ratio was between 1: 4 and 1: 1, the prepared product was composed of two phases (alpha-FeOOH and FeSO4OH center dot 2H(2)O). After hydrothermally aging the as-synthesized alpha-FeOOH nanorods at 180 degrees C for 1 d, alpha-Fe2O3 nanorods were obtained. However, the edge of the alpha-Fe2O3 nanorods was sword- like and different from the blunt edge of alpha-FeOOH nanorods due to a recrystallization mechanism.

Research on the mechanism of the formation of nanoparticle of α-Fe2O3 powder in aqueous solution with amorphous δ-FeOOH

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Studies on the Preparation of Alpha-Fe2o3 Ultrafine Particles by Microemulsion Reaction Method

Preparation and Catalytic Property of Single Crystal Multiporousα-Fe_2O_3 Nanorods

Hydrothermal synthesis and characterization of α-FeOOH and α-Fe2O3 uniform nanocrystallines

Morphology-controlled Synthesis of Α-Feooh and Its Derivatives

Preparation Of Alpha-Fe2o3 Hollow Spheres Via Random Aggregation Of Beta-Feooh Nanorods

Preparation and mechanism investigation of α-Fe2O3 with different morphologies

Synthesis and Properties of Nanocrystalline Δ-Feooh

Preparation and Characterization of Α-Feooh /Α-Fe2o3 Nanoparticles

Hydrothermal Synthesis and Characterization of Porous Hexagonal α-Fe2O3 Nanoparticles

Preparation and FTIR Spectra of Amorphous δ-FeOOH

Depositing of Amorphous Ferri-Oxide Nanoparticles on Surfaces of Submicron Aluminum Powder

Preparation of Nanometer-scale Α -Fe2o3 Particles Via a Complex Thermo-decomposition Method

Preparation of monodispersed α-Fe<sub>2</sub>O<sub>3</sub> nanoparticles by a hydrothermal synthetic route

Hydrothermal synthesis and characterization of monodisperse α-Fe2O3 nanocubes

Preparation of Nanoparticles and Hollow Spheres of Α-Fe2o3 and Their Properties

Synthesis of α-Fe2O3 nanoparticles via sonochemical hydrolysis

Fast Preparation, Characterization, and Property Study of α-Fe<sub>2</sub>O<sub>3</sub>Nanoparticles via a Simple Solution-Combusting Method

Large-scale synthesis and characterization of monodisperse Fe3O4 nanocrystals

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method