Abstract:Metallic (Cu/ZnO/Al2O3) and metal oxide (Fe2O3, Co3O4, NiO) catalysts are prepared by a facile alcohol solvent assisted method without additional aging and washing steps. In contrast to the conventional solid-state method using an oxalic acid/M2+ (M = metal cation) molar ratio as high as 4/1, this method is easily operated at room temperature, atmospheric pressure, and an oxalic acid/M2+ molar ratio of only 1.06/1, which prevents the release of lots of flammable gases from the decomposition of excessive oxalic acid. The effect of alcohol solvent types on the physicochemical properties of Cu/ZnO/Al2O3 catalysts and catalytic performance for low-temperature methanol synthesis is systemically studied. Using 1-propanol as solvent, the catalyst realizes an ultrahigh methanol yield of 1782.5 g/kgcat·h–1 at 220 °C and 5.0 MPa, much higher than most reported Cu-based catalysts for conventional high-temperature methanol synthesis. Besides, the Cu/ZnO/Al2O3 catalyst prepared by the alcohol solvent assisted method displayed much higher catalytic activity compared to other catalysts synthesized by conventional methods such as co-precipitation, impregnation, sol–gel, solid-state, and urea hydrolysis. Such good catalytic activity was due to the higher Cu0 surface area, smaller Cu crystallite size, greater surface basicity, and stronger H2 adsorption ability. This work provides not only a hopeful strategy for the large-scale fabrication of metallic and metal oxide catalysts but also a self-catalysis reaction pathway to achieve low-temperature methanol synthesis from CO and CO2 hydrogenation.

Stabilization of copper/zirconia based catalysts for alcohol synthesis

Strong Cu/ZnO Interfacial Interaction Induced by ZrO2 Promoter Suppressing the Ethanol Formation in Industrial Methanol Synthesis

Effect of La modified Cu/ZrO2 catalysts on alcohol synthesis

Structure and Catalytic Performance of Mn- and La-Modified Cu/Zro2 Catalysts for Methanol Synthesis

Development of highly stable catalyst for methanol synthesis from carbon dioxide

Effect of Preparation Method on the Performance of Cu‐Mn‐(La)‐Zr Catalysts for CO2 Hydrogenation to Methanol

Performance of Cu-Mn-Zn/ZrO2 catalysts for methanol synthesis from CO2 hydrogenation: The effect of Zn content

Stabilization of Cu/ZnO Based Catalysts by Nickel Additive in Methanol Decomposition

Modulation of Al2O3 and ZrO2 composite in Cu/ZnO-based catalysts with enhanced performance for CO2 hydrogenation to methanol

Synthesis of a Cu@ZnO1-x/Al2O3 Catalyst with High-Density ZnO1-x-Cu Interfacial Sites for Enhanced CO2 Hydrogenation to Methanol

Computational exploration of sub-nano Zn and Cu species on Cu/ZrO2: Implications for Methanol synthesis

Alcohol Solvent Assisted Synthesis of Metallic and Metal Oxide Catalysts: As-Prepared Cu/ZnO/Al 2 O 3 Catalysts for Low-Temperature Methanol Synthesis with an Ultrahigh Yield

Copper-doped ZnO-ZrO2 solid solution catalysts for promoting methanol synthesis from CO2 hydrogenation

Enhanced selectivity to methanol in CO2 hydrogenation on CuO/ZrO2 catalysts by alkali metal modification

Low temperature methanol synthesis in alcohol solvent over copper-based catalyst

Copper crystallite size and methanol synthesis catalytic property of Cu-based catalysts promoted by Al, Zr and Mn

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts

Synthesis, characterization and activity pattern of Cu–ZnO/ZrO2 catalysts in the hydrogenation of carbon dioxide to methanol

Methanol Synthesis from CO 2 Hydrogenation on CuO–ZnO–ZrO 2 Prepared by Solvothermal Method: the Influence of Solvent on Catalyst Properties and Catalytic Behavior

Sodium Hydroxide–Sodium Oxalate-Assisted Co-Precipitation of Highly Active and Stable Cu/ZrO 2 Catalyst in the Partial Oxidation of Methanol to Hydrogen

Effect of Lanthanum Promotion on the Unsupported Mo–Co–K Sulfide Catalysts for Synthesis of Mixed Alcohols from Syngas