Abstract:Metallic (Cu/ZnO/Al2O3) and metal oxide (Fe2O3, Co3O4, NiO) catalysts are prepared by a facile alcohol solvent assisted method without additional aging and washing steps. In contrast to the conventional solid-state method using an oxalic acid/M2+ (M = metal cation) molar ratio as high as 4/1, this method is easily operated at room temperature, atmospheric pressure, and an oxalic acid/M2+ molar ratio of only 1.06/1, which prevents the release of lots of flammable gases from the decomposition of excessive oxalic acid. The effect of alcohol solvent types on the physicochemical properties of Cu/ZnO/Al2O3 catalysts and catalytic performance for low-temperature methanol synthesis is systemically studied. Using 1-propanol as solvent, the catalyst realizes an ultrahigh methanol yield of 1782.5 g/kgcat·h–1 at 220 °C and 5.0 MPa, much higher than most reported Cu-based catalysts for conventional high-temperature methanol synthesis. Besides, the Cu/ZnO/Al2O3 catalyst prepared by the alcohol solvent assisted method displayed much higher catalytic activity compared to other catalysts synthesized by conventional methods such as co-precipitation, impregnation, sol–gel, solid-state, and urea hydrolysis. Such good catalytic activity was due to the higher Cu0 surface area, smaller Cu crystallite size, greater surface basicity, and stronger H2 adsorption ability. This work provides not only a hopeful strategy for the large-scale fabrication of metallic and metal oxide catalysts but also a self-catalysis reaction pathway to achieve low-temperature methanol synthesis from CO and CO2 hydrogenation.

Methanol Synthesis from CO2 Hydrogenation on CuO–ZnO–ZrO2 Prepared by Solvothermal Method: the Influence of Solvent on Catalyst Properties and Catalytic Behavior

Methanol Synthesis from CO 2 and H 2 over Pd/ZnO/Al 2 O 3 : Catalyst Structure Dependence of Methanol Selectivity

Solvothermal Preparation of CuO-ZnO-ZrO2 Catalysts for Methanol Synthesis Via CO2 Hydrogenation

Strong Cu/ZnO Interfacial Interaction Induced by ZrO2 Promoter Suppressing the Ethanol Formation in Industrial Methanol Synthesis

Performance of Cu-Mn-Zn/ZrO2 catalysts for methanol synthesis from CO2 hydrogenation: The effect of Zn content

Exploring the Effect of the Solvothermal Time on the Structural Properties and Catalytic Activity of Cu-ZnO-ZrO2 Catalysts Synthesized by the Solvothermal Method for CO2 Hydrogenation to Methanol

Development of highly stable catalyst for methanol synthesis from carbon dioxide

A practical approach for the preparation of high activity Cu/ZnO/ZrO2 catalyst for methanol synthesis from CO2 hydrogenation

PREPARATION OF CuO/ZnO CATALYST FOR METHANOL SYNTHESIS BY CARBON DIOXIDE HYDROGENATION I. Preparation Methods

High-Performance Cu/ZnO/Al 2 O 3 Catalysts for CO 2 Hydrogenation to Methanol

Methanol Synthesis from CO2 Hydrogenation with a Cu/Zn/Al/Zr Fibrous Catalyst

Preparing methods of CuO/ZnO/Al2O3 catalysts for the synthesis of methanol

Kinetics of Methanol Synthesis from Carbon Dioxide Hydrogenation over Copper–Zinc Oxide Catalysts

A High Activity Cu/ZnO/Al2O3 Catalyst for Methanol Synthesis: Preparation and Catalytic Properties

A highly efficient Cu/ZnOx/ZrO2 catalyst for selective CO2 hydrogenation to methanol

Preparation of Cu/ZnO/Al2O3 Catalysts in a Solvent-Free Routine for CO Hydrogenation

Alcohol Solvent Assisted Synthesis of Metallic and Metal Oxide Catalysts: As-Prepared Cu/ZnO/Al 2 O 3 Catalysts for Low-Temperature Methanol Synthesis with an Ultrahigh Yield

Inverse ZrO2/Cu as a highly efficient methanol synthesis catalyst from CO2 hydrogenation

Synthesis, characterization and activity pattern of Cu–ZnO/ZrO2 catalysts in the hydrogenation of carbon dioxide to methanol

Copper-doped ZnO-ZrO2 solid solution catalysts for promoting methanol synthesis from CO2 hydrogenation