Abstract:Fe-10%Ni alloys were synthesized in a high energy horizontal rotary ball mill from pure element Fe and Ni powders. Phase constitution, shape and thermal stability of the milled powders were characterized using X-ray diffractometry (XRD), scanning electron microscopy (SEM) and differential thermal analysis (DTA), respectively. And microstructure and properties of bulks prepared by hot-press sintering with milled powders as starting materials were analyzed and tested. Results indicate that under the condition of a milling speed of 400 r/min and a ball-to-powder mass ratio of 20:1, Ni fully solubilizes in Fe, which forms a supersaturate solid solution of Fe(Ni) with a body-centered cubic structure. Particles of the powder milled up to 16 h are more homogeneous and finer than those of the powder milled for 8 h, but phase of the powder is still Fe(Ni) solid solution. The alloy powder milled for 16 h were annealed in the temperature range between 500 and 800 degrees C. It is found that structure of the powder after annealing is stable and no phase transformation occurs in the powder. Phase of the powder is still Fe(Ni) solid solution. When the alloy powders milled for 16 h were treated by hot pressed sintering at 950 degrees C, a little Fe(Ni) solid solution with a face-centered cubic structure is found in the bulks. If the bulks that previously were treated by hot-press sintering at 950 degrees C and cooled to room temperature were subsequently sintered at 970 degrees C again, the phase of the powders completely transforms to Fe(Ni) solid solution with a face-centered cubic structure. However, the strength and ductility of bulks treated by hot-press sintering at 950 degrees C are superior to those of bulks by subsequent sintering at 970 degrees C, because oxide and holes are produced in resintered bulks without pressure.

Preparation of silver-nickel contact materials by mechanical alloying

Investigation of a Hot-Pressed Nb–Ti–Al Alloy: Mechanical Alloying, Microstructure and Mechanical Property

Microstructure and Arc Erosion Characteristics of Ag/Ni Contacts by Mechanical Alloying

An electrochemical investigation of mechanical alloying of MgNi-based hydrogen storage alloys

Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling

On the Preparation of Amorphous Mg–Ni Alloys by Mechanical Alloying

Microstructure and electrochemical properties of amorphous composites of ball-milled Mg2Ni0.95Sn0.05 + x wt% Ni

Minor Ni addition improving mechanical property of Au–20Ag–10Cu alloy

Research on Fe-10%Ni Alloy Synthesized by Mechanical Alloying

Study on the Mechanical Alloying Process for Preparing Ag/LSCO Electrical Contact Material

A Study about Fe-Ni Mechanical Alloying Process by Dry and Wet Method

Investigation of the Microstructure and Electrical Performance of Ag/SnO 2 In 2 O 3 Contacts with Nickel Addition Fabricated by Internal Oxidation

Preparation of Cbnp/Nicral Nanostructured Composite Powders by A Step-Fashion Mechanical Alloying Process

Formation of MgCNi3 and Mg–Ni Amorphous Mixture by Mechanical Alloying of Mg–Ni–C System

Mechanical alloying and direct powder forging of Ni–20Cr–20Fe-0.08C alloy

Nanophase Metallic Alloys Consolidated from Powders Prepared by Mechanical Alloying

Synthesis and Characterization of Nanoparticulate Strengthened Nickel Microcomponents

High-temperature surface alloying of nanocrystalline nickel produced by surface mechanical attrition treatment

Nanocrystalline Ni-30wt%Fe Supersaturated Solid Solution Synthesized by Mechanical Alloying

The Preparation of Silver-Coated Nickel Powders Via Electroless Plating

Microstructure and Mechanical Properties of Cu–12Al–xNi Alloy Prepared Using Powder Metallurgy