Abstract:(Zr62Cu15.4Ni12.6) (x = 6–12) in situ glassy composites containing uniformly distributed Ta-rich particles were prepared by arc-melting and copper mould casting. The results show that addition of 6–10 at.% Ta to Zr62Cu15.4Ni12.6Al10 results in dissolution of 2.4 to 4.6 at.% Ta in the glassy matrix, which promotes glass-forming ability, and the remaining Ta precipitates out as body-centered cubic (BCC) Ta-rich particles dispersed on the glassy matrix. The critical diameters for the composites with 6, 8, and 10 at.% Ta are 7, 7, and 6 mm, respectively. At 12 at.% Ta addition, the glass-forming ability is dramatically reduced because of the precipitation of secondary dendritic Ta-rich particles and other nanocrystallites from melts during copper mould casting. Also, owing to the solid-liquid reaction during induction heating, some Ta-rich particles formed in the master alloys will redissolve into the glassy matrix, resulting in a smaller volume fraction of Ta-rich particles in the as-cast glassy rods than that of the corresponding ingots. The glassy matrix composites exhibit enhanced plastic strain of about 7.5 to 22.5% at room temperature. The optimum Ta content in the glassy alloys is determined to be 10 at.%, which corresponds to the highest ultimate stress of 2220 MPa and the largest plastic strain of 22.5%. The plastic strain increases with increasing volume fraction of in situ BCC Ta-rich particles. This is apparently ascribed to the impedance of Ta-rich particles to shear bands. Ta-rich particles seed the initiation of multiple shear bands and block the shear band propagation, leading to intensive multiplication and bifurcation of shear bands.

Effects Of Ta, Nb And Mo Additions On Glass-Forming Ability Of Ti50ni20cu25sn5 Amorphous Alloy

Glass-forming ability and thermal stability of Gd55-xNd xCo20Al25 metallic glass

Effect of Ti addition on supercooled liquid region and glass forming ability of bulk amorphous Zr60Cu20Ni10-xAl10Tix alloys

Effects of Small Amount Ta on the Characteristics of the Zr-Al-Ni-Cu-Ta Bulk Metallic Glass

Thermal Stability and Mechanical Properties of Bulk Glassy Cu-Zr-Ti-(Nb, Ta) Alloys

EFFECT OF Ti ADDITION ON THE GLASS--FORMING ABILITY OF (Zr0.59cu0.18ni0.13al0.10)100-Xtix ALLOYS

Thermal stability and glass-forming ability of new Ti-based bulk metallic glasses

Effects of Ga,In additions of the Glass Forming Ability of Fe40Ni40P14B6 Eutectic Alloy

Effect of Ti addition on properties of Zr54Al10.2Ni9.4Cu26.4 glass forming alloy

Cu-alloying Effect on Crystallization Kinetics of Ti41Zr25Be28Fe6 Bulk Metallic Glass

Effects of Minor Additions on Ni- and Be-Free Ti-Based Bulk Glassy Alloys

Zr-Cu-Ni-Al-Ta Glassy Matrix Composites with Enhanced Plasticity

Effects of Alloying Elements on Crystallization Kinetics of Ti–Zr–Be Bulk Metallic Glass

Effects of the partial substitutional alloying elements on the crystallization behavior of Mg65Cu25Gd10 metallic glass: Ag versus Ni

Effect of Co Addition on the Glass-Forming Ability and Mechanical Properties of Ti-Zr-Be-Cu-Co Bulk Amorphous Alloys

Effects of minor Cu and Si additions on glass forming ability and mechanical properties of Co-Fe-Ta-B Bulk metallic glass

Effects of Ta Addition on the Microstructure, Compression Properties and Oxidation Resistance of NiAl-Cr(Mo) Alloy

Glass-forming Ability and Thermal Stability of Fe-Co-Ni-Zr-Mo-W-B Bulk Amorphous Alloys

Effects of Al on Glass-Forming Ability and Thermal Stability of Cu-Based Metallic Glass

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

The Effect of Ni Substitution on the Glass-Forming Ability and Mechanical Properties of Mg–Cu–Gd Metallic Glass Alloys