Abstract:Zr50Cu34-xFexAl8Ag8 (x = 0, 2, 4, 6, and 8) alloy bars of different diameters were prepared by copper mold suction casting and copper mold casting. The compressive mechanical properties of metallic glass samples with different Fe contents were determined by a universal testing machine. The microstructure and thermodynamics of the alloy samples were analyzed by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and differential scanning calorimetry. According to the experimental results, Fe doping had a significant effect on the glass-forming ability, stability, and mechanical properties of these metallic glasses. The maximum diameter of the Zr50Cu32Fe2Al8Ag8 metallic glass bar was 15 mm, and the cooling rate of the alloy sample was 7.7 K/s. The addition of Fe inhibited the formation of stable crystalline phases inside the alloy sample and improved the glass-forming ability of the metallic glass. With the addition of Fe, the DSC curve of the alloy sample moved to higher temperatures, and the characteristic temperatures and the stability of the metallic glass increased. The fracture strength (σmax) and ultimate strain (εf) of the metallic glass samples reached their maximum values of 1917.6 MPa and 3.97 %, respectively, for Zr50Cu30Fe4Al8Ag8. Compared with the Fe-free Zr50Cu34Al8Ag8 metallic glass, σmax and εf increased by 51.4 MPa and 1.19 %, respectively. With the addition of Fe, the change in the distribution and content of free volume inside the metallic glass sample is the main reason for the improvement of its mechanical properties. This study shows that trace element doping has an important effect on the properties of metallic glasses.

Effects of minor Cu and Si additions on glass forming ability and mechanical properties of Co-Fe-Ta-B Bulk metallic glass

Effect of Co Addition on the Glass-Forming Ability and Mechanical Properties of Ti-Zr-Be-Cu-Co Bulk Amorphous Alloys

Effects of Cu Additions on Mechanical and Soft-Magnetic Properties of CoFeBSiNb Bulk Metallic Glasses

The Effect of Co Addition on Glassy Forming Ability and Soft Magnetic Properties of Fe-Si-B-P Bulk Metallic Glass

Effects of Minor Additions on Ni- and Be-Free Ti-Based Bulk Glassy Alloys

The effect of minor alloying on the glass forming ability and crystallization reaction of Ti32.8Zr30.2Cu9M5.3Be22.7 (M=Fe, Co, and Ni) bulk metallic glass

Effect of Cu addition on the GFA, structure and properties of Fe-Co-based alloy

Effect of partial substitution of Cr with Co on glass forming ability, mechanical and magnetic properties in Fe48Mo14Cr15-xCoxB6P8Si7Y2 bulk metallic glasses

Effects of Ga,In additions of the Glass Forming Ability of Fe40Ni40P14B6 Eutectic Alloy

Synthesis,structure and Mechanical Properties of Zr-Cu-based Bulk Metallic Glass Composites

Effects of Fe Addition on Glass-Forming Ability and Mechanical Properties of Ti–Zr–Be Bulk Metallic Glass

Effects of Co Substitution for Fe on the Glass Forming Ability and Properties of Fe80P13C7 Bulk Metallic Glasses

Effect of Nb Addition on the Glass-Forming Ability, Soft-Magnetic Properties and Mechanical Properties of CoFeNiBSiNb Bulk Glassy Alloys

Effect of Fe addition on the glass-forming ability, stability, and mechanical properties of Zr50Cu34-xFexAl8Ag8 metallic glasses

Fe–C micro-alloying effect on properties of Zr53Al11.6Ni11.7Cu23.7 bulk metallic glass

Cu-alloying Effect on Crystallization Kinetics of Ti41Zr25Be28Fe6 Bulk Metallic Glass

Centimeter-sized Ti-based Bulk Metallic Glass with High Specific Strength

Effects of Cr addition on glass-forming ability and mechanical properties of Cu–Zr–Al bulk metallic glass

Effect of Al addition on properties of Cu45Zr45.5Ti9.5 bulk metallic glass

Effects of Al on Glass-Forming Ability and Thermal Stability of Cu-Based Metallic Glass

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses