Abstract:Abstract Nickel-based alloy coatings were widely used for the remanufacturing of dies and moulds by laser cladding, but the crack sensitivity would be increase due to the higher strength and hardness, which reduced the wear resistance of Ni-based alloys. In this paper, Ni-based coatings with the addition of a plastic phase (an austenitic stainless net) were prepared using laser cladding technology, and the CeO 2 was added in cladding layers. The cracking mechanism, microhardness, microstructure, phase composition, and wear properties were investigated. The relationship between thermal stress and the elastic and plastic fracture had been developed from the standpoint of fracture mechanics and thermal elastic fracture mechanics. The fracture criterion of the nickel-based coating was obtained, and the study has shown that the crack sensitivity could be reduced by decreasing the thermal expansion coefficient Δ α . Thus, a new method was proposed, which the stainless steel nets were prefabricated on the substrate. It was found that the number of cracks reduced significantly with the addition of stainless steel net. When the stainless steel net with 14 mesh was added in Ni-based coatings, the average microhardness of nickel composite coating was 565 HV 0.2 , which was 2.6 times higher than that of the 45 steel substrate. Although the rare earth oxide 4 wt.% CeO 2 and stainless steel net were added in the Ni-based coating reducing the microhardness (the average microhardness is 425 HV 0.2 ), the wear resistance of it improved substantially. The wear volume of Ni-based composite coating was 0.56×10 −5 mm 3 ·N −1 ·m −1 , which was 85.1% lower than that of 45 steel. The experiment results have shown that the Nickel-based composite coating is equipped with low crack sensitivity and high abrasive resistance with austenitic stainless net and the rare earth oxide 4 wt.% CeO 2 . This research offers an efficient solution to produce components with low crack susceptibility and high wear-resistance coatings fabricated by laser cladding.

Crack resistance and wear resistance of laser clad layer on the surface of cast iron

Development of Laser Cladding Materials with Crack Resistance and Wear Resistance in Clad Layer of Grey Iron

A Study on the Wear Resistance of Laser Cladding Layers on Grey Iron

Effect of Nodulation of Eutectic Carbides on Crack Resistance of Laser-Clad Layers on Cast Iron

Microstructure and Wear Resistance of Ductile Cast Iron Laser Clad with Ni-Ti-Co-C

Effect of Cu-Ni-V-C Alloy on Properties of Laser Clad Layer

Study of the effect of overlap rate on the failure form, microstructure and wear resistance of multilayer laser cladding on grey cast iron surfaces

Properties of Laser-Clad Stainless Steel–Ni/WC Double-Layer Coatings

Study of the Microstructure and Corrosion Properties of a Ni-Based Alloy Coating Deposited onto the Surface of Ductile Cast Iron Using High-Speed Laser Cladding

Numerical Optimization and Performance Study of Ni-Based Coatings on Gray Cast Iron Surface by High-Speed Laser Cladding Based on Orthogonal Test

The Effect of TiC-Fe3C on the Wear Resistance of Laser Cladding Layers in Grey Iron

Study on ductile iron surface laser cladding austenitic stainless steel coating heat treatment to enhance wear resistance

TiC Reinforcement Composite Coating Produced Using Graphite of the Cast Iron by Laser Cladding

Repair feasibility and performance enhancement analysis of Fe-based alloy coating on ductile iron surface by high-speed laser cladding

Research on the Thermal Fatigue Mechanism of Laser Cladding IN625 Process on Ductile Iron

Study on Cracks in Laser Direct-Cladded Titanium Layer on Low Carbon Steel

Study on the microstructure and wear resistance of laser cladding layer of Ni and Cr on the surface of stainless steel

Microstructural evolution and corrosion properties of Ni-based alloy coatings fabricated by multi-layer laser cladding on cast iron

Study on the mechanism and correlation of double-pit pitting in ductile iron IN625 laser cladding layer

Research on Laser Cladding Co-Based Alloy on the Surface of Vermicular Graphite Cast Iron

Study of Cracking Mechanism and Wear Resistance in Laser Cladding Coating of Ni-based Alloy