Abstract:In order to study the microstructure and property of cobalt based alloy layer cladding on the surface of ductile cast iron QT600-3 by laser, laser cladding of CoCrW alloy powder with the particle size of 46~106μm on the surface of QT600-3 was performed by 6 kW CO2 laser.Laser cladding process parameters were:laser power P=3.0 kW, scanning speed V=350 mm· min-1 , laser spot diameter 2 mm, lap ratio 1.5, three pass cladding, for which the thickness of cladding layer was about 3 mm.The temperature distri-bution of the cast iron sample was adjusted and controlled by the heat compensation during laser cladding processing.The microstruc-ture, composition, phases and hardness on the cross section of the cladding layer were investigated by Olympus metallurgical micro-scope ( OM) , Zeiss-Sigma scanning electron microscope ( SEM) , X′Pert MPD Pro X-ray diffraction ( XRD) and MHV2000 digital mi-cro hardness tester and the hardness changing was analyzed.The results showed that, the surface quality of the cladding layer was fine without crack, porosity and other defects;the cladding layer could be divided into melting zone, combined zone and heat affected zone, and it was integrated metallurgically with the ductile cast iron matrix, which was mainly composed ofγ-Co ( face centered cubic) solid solution and carbide of CoCx , Cr7 C3 , etc.The melting zone consisted of a surface layer of dendritic crystals and an internal layer of cellular crystals, and the transformation to the plate martensite occurred in the heat affected zone, where the globular graphite partially dissolved to the smaller graphite.The hardness of the cross section of the cladding layer increased rapidly and then increased gently with the increase of the distance from the surface of the graphite cast iron matrix, finally in the surface area rapidly increased.The maximum hardness of the cladding layer was HV0.21077, which was up to 4 times higher than that of the substrate of ductile cast iron.

A Study on the Wear Resistance of Laser Cladding Layers on Grey Iron

Development of Laser Cladding Materials with Crack Resistance and Wear Resistance in Clad Layer of Grey Iron

Crack resistance and wear resistance of laser clad layer on the surface of cast iron

The Effect of TiC-Fe3C on the Wear Resistance of Laser Cladding Layers in Grey Iron

Study on Friction and Wear of Cast Iron Friction Surface Layer by Laser Cladding

Microstructure and Wear Resistance of Ductile Cast Iron Laser Clad with Ni-Ti-Co-C

Numerical Optimization and Performance Study of Ni-Based Coatings on Gray Cast Iron Surface by High-Speed Laser Cladding Based on Orthogonal Test

TiC Reinforcement Composite Coating Produced Using Graphite of the Cast Iron by Laser Cladding

Research on Laser Cladding Co-Based Alloy on the Surface of Vermicular Graphite Cast Iron

Study of the Microstructure and Corrosion Properties of a Ni-Based Alloy Coating Deposited onto the Surface of Ductile Cast Iron Using High-Speed Laser Cladding

Study of the effect of overlap rate on the failure form, microstructure and wear resistance of multilayer laser cladding on grey cast iron surfaces

Microstructure and Soil Wear Resistance of a Grey Cast Iron Alloy Reinforced with Ni and Cr Laser Coatings

Properties of Laser-Clad Stainless Steel–Ni/WC Double-Layer Coatings

Microstructural Properties of Particle-Reinforced Multilayer Systems of 316L and 430L Alloys on Gray Cast Iron

Microstructure and Property of Laser Cladding Cobalt Based Alloy Coatings on Ductile Cast Iron

Laser Cladding In Situ Carbide-Reinforced Iron-Based Alloy Coating: A Review

Microstructure and Wear Resistance of High-Chromium Cast Iron with Multicomponent Carbide Coating via Laser Cladding

Fe-Cr-Si-B coating by laser cladding on nodular cast iron

Microstructure, phase composition and wear properties of iron-based gradient coatings by laser cladding on 65Mn steel

Comparative Study on the Microstructure, Wear Behavior, and Corrosion Performance of Iron-Based and Cobalt-Based Coatings Fabricated by Laser Cladding

Microstructure Evolution During Laser Cladding Fe-Cr Alloy Coatings on Ductile Cast Iron