CALPHAD-guided alloy design of Bi-modified Al–Sn bearing alloy with multiphase composite structure and optimal self-lubricating property
Bowen Dong,Zhenpeng Wu,Pengfei Wang,Chao Ke,Shichao Liu,Jinchuan Jie
DOI: https://doi.org/10.1016/j.jallcom.2021.159756
IF: 6.2
2021-09-01
Journal of Alloys and Compounds
Abstract:<p>Through primary phase diagram analysis and thermodynamic calculation of Al–Sn, Al–Bi and Sn–Bi binary systems, Bi element was ensured to be a suitable alloying element possibly introducing granular Bi-rich precipitates and increasing the self-lubricating property of Al–Sn bearing alloy. Through calculation of excess free energy of liquid (<span class="math"><math>Gexcessliq</math></span>) in Al–Sn–Bi ternary system, it's further proven that the segregation of Bi in Al can be suppressed by Sn element. Pseudo-binary phase diagrams of Al–Sn–xBi (wt%, x = 0, 1, 2, 3) were obtained through CALPHAD method, it's found that Al–20Sn and Al–20Sn–1Bi alloys are composited of α-Al and Sn-rich secondary phases (SPs). However, Bi will be precipitated from the Sn-rich SPs in Al–20Sn–2Bi and Al–20Sn–3Bi alloys which are thus composited of three phases (α-Al, Sn-rich SPs and Bi-rich precipitates). The Al–20Sn–xBi (wt%, x = 0, 1, 2, 3) alloys were prepared with the guidance of CALPHAD. The microstructures match the calculation results well, fine and granular Bi-rich precipitates can be observed only in Al–20Sn–2Bi and Al–20Sn–3Bi alloys. Friction coefficients of alloys firstly decrease to 0.23 and then increase to 0.32 with Bi content increasing from 0 wt% to 3 wt%. The granular Bi-rich precipitates can improve the self-lubricating property of Al-Sn alloy. However, the increasing brittleness will lead to decrease of self-lubricating property when Bi content surpasses the critical value.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering