Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Synthesis of Nanoparticles with Thermal Hydrolyzationand Its Dispersion on Si Surface

Controllable Synthesis of SiO2 Nanoparticles: Effects of Ammonia and Tetraethyl Orthosilicate Concentration

Influence of Different Preparation Methods on Crystallisation and Morphology of Fe2o3 Nanoparticles

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Synthesis of Ag/SiO2 nanocomposite material by adsorption phase nanoreactor technique

Controllable Synthesis of (nh4)fe2(po4)2(oh)·2h2o Using Two-Step Route: Ultrasonic-intensified Impinging Stream Pre-Treatment Followed by Hydrothermal Treatment.

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Effects on Direct Synthesis of Large Scale Mono-Disperse Ni0.5zn0.5fe2o4 Nanosized Particles

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

Synthesis of Uniform Ferric Oxide Particles from Deionized Colloids

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Hydrothermal synthesis of monodisperse α-Fe2O3 nanocubes

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Modification of Nanosilica Particles with Hydrophobic Modifier Bis[3-(Triethoxysilyl)propyl]tetrasulfide by Using Micro-Injection in Aqueous Solutions

Hydrothermal synthesis and characterization of α-FeOOH and α-Fe2O3 uniform nanocrystallines

Preparation and Surface Modification of Fe<sub>3</sub>O<sub>4 &Lt;/sub>nano-Magnetic Powders

Synthesis and Characterization of Monodisperse Hollow SiO2 Nanospheres

Size-controlled syntheses and hydrophilic surface modification of Fe 3O4, Ag, and Fe3O4/Ag heterodimer nanocrystals