Interface characteristic and mechanical performance of TiAl/Ti2AlNb diffusion bonding joint with pure Ti interlayer
Lei Zhu,Bin Tang,Ming-Xuan Ding,Yan Liu,Xiao-Fei Chen,Shao-Peng Yan,Jin-Shan Li
DOI: https://doi.org/10.1007/s12598-020-01548-5
IF: 6.318
2020-09-02
Rare Metals
Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">Solid-state diffusion bonding (DB) of TiAl alloy and Ti<sub class="a-plus-plus">2</sub>AlNb alloy was carried out using pure Ti as an interlayer at 1000 °C under 20 MPa for 60–120 min. The effects of bonding times on the interfacial microstructure and mechanical performance of the TiAl/Ti/Ti<sub class="a-plus-plus">2</sub>AlNb bonded joints at room temperature (RT) were investigated detailly. The results demonstrated that the diffusion layers (DLs) mainly consisted of four characteristic layers, (I) single coarse α<sub class="a-plus-plus">2</sub> phase adjacent TiAl alloy, (II) single refined α<sub class="a-plus-plus">2</sub> phase at the bonding interface, (III) equiaxed/acicular α<sub class="a-plus-plus">2</sub> phase embedded in β phase adjacent Ti<sub class="a-plus-plus">2</sub>AlNb alloy and (IV) both equiaxed α<sub class="a-plus-plus">2</sub> phase and acicular O phase embedded in β phase adjacent Ti<sub class="a-plus-plus">2</sub>AlNb alloy, respectively. The thickness of the four layers increased with the increasing of the bonding time. The growth of DLs is controlled by diffusion and the reaction rate constant <em class="a-plus-plus">k</em> for region I, II, III and IV are 1.22 × 10<sup class="a-plus-plus">−6</sup>, 1.27 × 10<sup class="a-plus-plus">−6</sup>, 2.6 × 10<sup class="a-plus-plus">−7</sup> and 7.7 × 10<sup class="a-plus-plus">−7</sup> m·s<sup class="a-plus-plus">−1/2</sup>, respectively. Meanwhile, the interface α<sub class="a-plus-plus">2</sub> grain grows up without texture. The maximum tensile strength of 281 MPa was maintained at 1000 °C for 90 min under the pressure of 20 MPa. Consequently, the phase transformation and dynamic recrystallization behavior of the DLs were discussed.</p></span><span class="a-plus-plus abstract-section id-a-sec2 outputmedium-online"><h3 class="a-plus-plus">Graphic abstract</h3></span>
materials science, multidisciplinary,metallurgy & metallurgical engineering