INTERFACE STRUCTURE AND BOND STRENGTH OF DIFFUSIONG -BONDED JOINT OF TiAl-BASE ALLOY TO 40Ct STEEL
Peng He,Jicai Feng,Binggang Zhang,Yiyu Qian,Delun Guo,Jinbao Hou
DOI: https://doi.org/10.3969/j.issn.1001-1382.2000.12.005
2000-01-01
Abstract:TiA1 alloy was diffusion bonded to 40Cr steel in vacuum furnace. Results showed, at the TiA1 -40Cr inter face, the reaction layer of mixture was formed closest to TiA1 base, TiC layer was formed in the middle and obvious decarbonised layer was formed closest to 40Cr steel side. The widths of the three reaction layer increased with the increase of the bond temperature and the bond time. The ambient ultimate tensile strengths of the tested joints were poor, and fractography revealed that all joints fractured in the TiC layer, producing brittle cleavage fracture surface. High bond temperature and short bong time was propitious to decresing metallic compounds resulting in brittleness of the weld joint and obtaining high good properties of bonding.