Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

INITIATION AND PROPAGATION OF FATIGUE CRACK INEDGE REGION OF HOLE IN A SHEET WITH CENTRAL HOLE

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of Initial Overload on the Low Cycle Fatigue Life of Gh4169 Alloy at Different Temperatures

Quantitative Study of High-Frequency Fatigue Hole-Edge Stresses in Nickel-Based Single-Crystal Superalloy

Fatigue crack nucleation behavior in nickel-based PM alloy

Study of Fatigue Crack Initiation and the Propagation Mechanism Induced by Pores in a Powder Metallurgy Nickel-Based FGH96 Superalloy

Investigations of micro-notch effect on small fatigue crack initiation behaviour in nickel-based alloy GH4169: Experiments and simulations

Effect of Stress Ratio on the Fatigue Crack Propagation Behavior of the Nickel-based GH4169 Alloy

Effects of Distance and Alignment Holes on Fatigue Crack Behaviors of Cast Magnesium Alloys

Influence of Multi-Holes on Fatigue Behaviors of Cast Magnesium Alloys Based on In-Situ Scanning Electron Microscope Technology

Creep-fatigue rupture mechanism and microstructure evolution around film-cooling holes in nickel-based DS superalloy specimen

The Test of Low Cycle Fatigue Characteristics for 45CrNiMoVA Steel and In-situ Observation on Surface Crack Propagation

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Fracture Mechanisms Induced by Microporosity and Precipitates in Isothermal Fatigue of Polycrystalline Nickel Based Superalloy

Fatigue Life Prediction of Nickel-Based GH4169 Alloy on the Basis of a Multi-Scale Crack Propagation Approach

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Failure mechanism and life correlation of Inconel 718 in high and very high cycle fatigue regimes

Fatigue life assessment of nickel-based single crystals considering equivalent initial flaw size model and anisotropy

Fatigue Crack Initiation Potential from Defects in Terms of Local Stress Analysis

Small Fatigue Crack Initiation and Growth Mechanisms of Nickel-Based Superalloy GH4169 at 650 °C in Air

Quantitative Relationship Between Weld Defect Characteristic and Fatigue Crack Initiation Life for High-Cycle Fatigue Property