Effect of HIP on precipitations and tensile properties of directionally solidified NiAl/Cr(Mo,Hf) alloy

Jianting Guo,Chuanyong Cui,Yihui Qi,Yuxi Chen,Hengqiang Ye
2002-01-01
Abstract:The precipitations and the high temperature tensile strength of DS NiAl/Cr(Mo, Hf) alloy after the HIP and aging treatment were studied. The experimental results showed that the NiAl and Cr(Mo) eutectic phases were stable, while the Heusler phase, which was distributed at the NiAl/Cr(Mo) interface in the as-cast alloy, was reduced greatly and redistributed in the NiAl and Cr(Mo) phases. It was also found that the Heusler particles mainly precipitated at the NiAl/Cr(Mo) interface and NiAl grain boundaries, the reason of which was interpreted from the viewpoint of interfacial energy. The G-phase also disappeared in the HIPed and aged specimen. The tensile experiments showed that the strength of the alloy was higher than that of most NiAl-based alloys.