Precipitation and Coarsening Kinetics of H-phase in NiTiHf High Temperature Shape Memory Alloy

A. Shuitcev,Y. Ren,B. Sun,G. V. Markova,L. Li,Y. X. Tong,Y. F. Zheng
DOI: https://doi.org/10.1016/j.jmst.2021.11.011
2022-01-01
Journal of Material Science and Technology
Abstract:Precipitate hardening is the most easiest and effective way to enhance strain recovery properties in NiTiHf high-temperature shape memory alloys. This paper discusses the precipitation, coarsening and age hardening of H-phase precipitates in Ni 50 Ti 30 Hf 20 alloy during isothermal aging at temperatures between 450 degrees C and 650 degrees C for time to 75 h. The H-phase mean size and volume fraction were determined using transmission electron microscopy. Precipitation kinetics was analyzed using the JohnsonMehl-Avrami-Kolmogorov equation and an Arrhenius type law. From these analyses, a Time-TemperatureTransformation diagram was constructed. The evolution of H-phase size suggests classical matrix diffusion limited Lifshitz-Slyozov-Wagner coarsening for all considered temperatures. The coarsening rate constants of H-phase precipitation have been determined using a modified coarsening rate equation for nondilute solutions. Critical size of H-phase precipitates for breaking down the precipitate/matrix interface coherency was estimated through a combination of age hardening and precipitate size evolution data. Moreover, time-temperature-hardness diagram was constructed from the precipitation and coarsening kinetics and age hardening of H-phase precipitates in Ni 50 Ti 30 Hf 20 alloy. (c) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
What problem does this paper attempt to address?