Abstract:The contradiction between strength and ductility limits the application of high-entropy alloys (HEAs). To simultaneously improve the strength and ductility of HEAs, the cryogenic treatment was proposed and applied in this paper. The Al0.6CrFe2Ni2 HEA with dual-phase structure was selected as the experimental material for cryogenic treatment. The microstructure and mechanical properties of the HEA in an as-cast and cryogenically treated state were analyzed in detail. The results showed that the grain size of equiaxed crystal in the alloy decreased continuously by prolonging the cryogenic treatment time, and the average value was 44.6 μm for the cryogenically treated HEA at the time of 48 h, which was 46.5% lower than that of the as-cast alloy. The number and size of ordered body-centered cubic (B2) spherical nanophases embedded in the body-centered cubic (BCC) structured inter-dendritic region, however, increased continuously by extending the cryogenic treatment time. The cryogenic treatment also made more slip systems activate, cross-slip occurred in the alloy, and a large number of stacking faults were found in the transmission electron microscopy (TEM) microstructure for the alloy that underwent a long time in cryogenic treatment. The yield strength of the Al0.6CrFe2Ni2 HEA was gradually increased with the increase in cryogenic treatment time, and the maximum yield strength of the 48 h cryogenically treated alloy was 390 MPa, which was 39.3% higher than that of the as-cast. This increase in mechanical properties after cryogenic treatment was attributed to the refinement of grains and the large precipitation of nanophases, as well as the appearance of cross-slips and stacking faults caused by cryogenic treatment.

Effect of heat treatment on hydrogen embrittlement susceptibility of Al 0.25 CoCrFeNi high entropy alloy

Immunity of Al0.25CoCrFeNi high-entropy alloy to hydrogen embrittlement

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

Effect of Heat Treatment on the Microstructure and Mechanical Properties of the Al0.6CoCrFeNi High-Entropy Alloy

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Study on Precipitation in (cocrfemnni)90al6ti4 High Entropy Alloy

Hydrogen embrittlement of a precipitation-strengthened high-entropy alloy

Effect of Annealing on Microstructure Evolution and Tensile Behavior of Hot-Rolled FeMnCoCrAl High-Entropy Alloy

Microstructure evolution and mechanical behavior of a CoCrFeNiMn0.75Cu0.25 high-entropy alloy by thermo-mechanical treatment

Hydrogen embrittlement of additively manufactured AlCoCrFeNi2.1 eutectic high-entropy alloy

Effect of Cold Deformation and Heat Treatment on the Microstructure and Mechanical Behavior of High Entropy Alloy CuCrFeNi2Al0.5

Effect of annealing treatment on microstructural evolution and compressive behavior of Al0.5CrFeNi2.5Si0.25 high-entropy alloy

Effect of hydrogen charging time on hydrogen embrittlement of CoCrFeMnNi high-entropy alloy

Effect of Heat Treatment on the Microstructure and Corrosion Resistance of Al0.75CoCr1.25FeNi High-Entropy Alloys

Effect of Cryogenic Treatment on Microstructure and Mechanical Properties of Al0.6CrFe2Ni2 Dual-Phase High-Entropy Alloy

Study on the Effect of Aging Treatment on the Microstructure and Properties of Fe24Co27Ni32Cr8Al6Ti3 High-Entropy Alloy

Effect of Intercritical Annealing Time on Hydrogen Embrittlement of Warm-Rolled Medium Mn Steel

Effect of annealing on mechanical and thermoelectric properties of a Al2CoCrFeNi high-entropy alloy

Microstructural evolution, mechanical and corrosion behavior of an Al7.5Co20.5Fe24Ni24Cr24 high‐entropy alloy

Hydrogen Embrittlement of CoCrFeMnNi High-Entropy Alloy Compared with 304 and IN718 Alloys

Microstructural Evolution and Tensile Properties of Al0.3CoCrFeNi High-Entropy Alloy Associated with B2 Precipitates