PRFCONDITIONS OF THE HARMFUL EFFECT INDUCED BY DELAYED ETTRINGITE FORMATION IN MASSIVE SHRINKAGE-COMPENSATING CONCRETE

Peiyu Yan,Jiang PENG,Xiao Qin

DOI: https://doi.org/10.3321/j.issn:0454-5648.2001.02.003

2001-01-01

Abstract:The preconditions of the harmful effect induced by delayed ettringite formation (DEF) in massive shrinkage- compensating concrete whose binder is composed of portland cement and expansive agent were studied. The phase composition of hydration product was determined with semi-quantitative step-scanning XRD and the restrained expansion of mortars was measured. It is found that the shrinkage- compensating concrete going through high temperature in the early age was sensitive to the environmental humidity alternation in the later stage. Only cured in an appropriate humid condition, an appropriate expansion of mortars with suitable strength can be obtained to remedy the adverse effect of the expansion loss in the early age. It is important to note that the shrinkage - compensating concrete structure that goes through high temperature in early age and is cured in undue dry or humid environment in later age may suffer shrinkage cracking or expansion damage. In high strength concrete, especially, only a small quantity of later formed ettringite in the dense paste can induce concentration of stress and results in cracking of concrete. It is very important for the construction of massive shrinkage compensating concrete that effectively controlling the core temperature of concrete under a threshold.