Microstructures and mechanical properties of TA1 sintered samples prepared by injection molding using water-soluble binder
Weichen Zhang,Lu Li,Peng Cao,Gang Chen,Muhammad Dilawer Hayat,Weichen ZhangLu LiPeng CaoGang ChenMuhammad Dilawer Hayata Faculty of Material Science and Engineering,Kunming University of Science and Technology,Kunming,P. R. Chinab Research Center for Analysis and Measurement,Kunming University of Science and Technology,Kunming,P. R. Chinac Faculty of Engineering,Chemical and Materials Engineering,University of Auckland,Auckland,New Zealandd Faculty of Material Science and Engineering,University of Science and Technology Beijing,Beijing,P. R. Chinae Faculty of Engineering,University of Waikato,Hamilton,New Zealand
DOI: https://doi.org/10.1080/01694243.2024.2320502
IF: 2.431
2024-02-29
Journal of Adhesion Science and Technology
Abstract:A water-soluble binder was used to obtain TA1 sintered samples prepared by injection molding. The effects of the sintering temperature on the microstructures and mechanical properties of the sintered samples were analyzed. A relative density of >91% is achieved. Some residual carbon and oxygen remain in the sintered samples, affecting the mechanical properties. The tensile strength and elongation of the sample sintered at 1,300 °C are the highest: 592 MPa and 12.95%, respectively. Detailed electron microscopic analysis was performed to identify the morphology and nature of the resultant titanium carbides and oxides.
materials science, multidisciplinary,engineering, chemical,mechanics