Abstract:This study aimed to fabricate zirconia-alumina composites via powder injection molding and investigated the effects of alumina addition on microstructure as well as physical properties of the composites. Zirconia-alumina composites were prepared using polyethylene glycol (PEG) and polyvinyl butyral (PVB) as binders. The powder loading was fixed at 38 vol%, and PEG: PVB binder weight ratio was fixed at 80:20. Alumina content within ceramic component was varied at 0, 10, 20, 30, 40 and 50 vol% to observe the effect of alumina on the composite structures and properties. The injection molding was done at 190°C followed by water debinding of PEG at 40°C. Thermal debinding of PVB at 450°C was performed prior to sintering at 1450°C. From the density measurement via Archimedes’ method, the relative density of sintered samples was found to be highest at 10 vol% alumina and gradually lower at higher alumina content. The condition with highest density yielded the highest flexural modulus and flexural strength. XRD indicated that tetragonal zirconia phase coexisted with alumina when alumina was added. Above 20 vol% alumina, monoclinic zirconia was also detected. The increased porosity in samples with high alumina content, as confirmed in SEM morphological observation, correlated with lower flexural strength and lower flexural modulus. The results illustrated the feasibility of powder injection molding in the production of zirconia-alumina composites and the optimum condition in this study was 10 vol% alumina.

Injection molding of ultra-fine zirconia (Y-TZP) powders

Injection Molding of Oxide Ceramic with High Performance

The Effect of Organic Vehicle on the Injection Molding of Ultra-Fine Zirconia Powders

Injection Molding Process and Microstructure of Ceramic Micro-Structured Part

Control of the Surface Quality for ZrO_2 Microstructures by Powder Micro-Injection Molding

Surface Modification of the Zirconia Powders for Injection Molding

Injection Molding of Ultra-Fine Si 3 N 4 Powder for Gas-Pressure Sintering

A Strategy to Obtain a High-Density and High-Strength Zirconia Ceramic Via Ceramic Injection Molding by the Modification of Oleic Acid

Injection Molding of Zirconia Ceramics Using Water-Soluble Binder

Surface Features of Polymer and Ceramic Microstructured Parts Manufactured by Micro Injection Molding

Study of Factors Influencing the Microstructure and Phase Content of Ultrafine Y-Tzp

Microstructure and properties of zirconia-alumina composites fabricated via powder injection molding

Additive manufacturing of dense zirconia ceramics by fused deposition modeling via screw extrusion

Fused deposition fabrication of high-quality zirconia ceramics using granular feedstock

Fabrication of Porous Zirconia Ceramics by Injection Molding Method

Study on the characteristics of injection molding green bodies of ZrO 2 ceramics

Surface-modified by coupling agent and injection molding of zirconia powder

Debinding behaviour and sintering temperature-dependent features of coloured zirconia fabricated by ceramic injection moulding

[Influence of Compaction Pressure and Pre-Sintering Temperature on the Machinability of Zirconia Ceramic].

Effects of Different Backbone Binders on the Characteristics of Zirconia Parts Using Wax-Based Binder System Via Ceramic Injection Molding

Study on the characteristics of injection molding green bodies of ZrO2 ceramics