Abstract:<p>Thermal and autogenous deformations of high-performance concrete at early ages have significant impact on the performance, serviceability, and durability of concrete structures. While substantial past research has significantly improved our fundamental understanding of the autogenous shrinkage and of the coefficient of thermal expansion (CTE) of cement paste and mortar, such understanding for concrete, especially modern types of high-performance concrete at early ages, remains inadequate. Accordingly, a new Temperature Stress Testing Machine (TSTM) capable of generating reliable data on autogenous shrinkage and CTE of concrete from very early ages has been built. After a review of relevant major aspects, key features of the newly-built TSTM are reported, with a focus on advanced thermal regulation and deformation capturing systems. The outcomes of a study using the newly-developed TSTM on autogenous deformation and CTE of early-age concrete (two mixtures with water-to-binder ratio of 0.35 and 0.42) subject to different curing temperatures (23, 35 and 45 °C) are then presented. Higher curing temperatures significantly accelerate the development of autogenous shrinkage at very early ages, whereas after the initial period, the magnitude of autogenous shrinkage cured at the intermediate temperature of 35 °C gradually becomes the largest. Despite this cross-over, the maturity concept appears appropriate to approximate the effect of curing temperature on autogenous shrinkage of concrete at early ages. The linear CTE of early-age concrete, obtained using stepped temperature profiles follows a clear rising trend after setting. Based on the newly-measured CTE, an attempt was made to separate thermal strain and self-desiccation shrinkage, in which the presence of non-negligible delayed thermal strain became evident.</p>

Study on Experimental Method for Determining Autogenous Volume Deformation and Its Application

Optimization of Autogenous Volume Deformation Process Curve of MgO Concrete

Experimental and Theoretical Studies on Autogenous Shrinkage of Concrete at Early Ages

Experimental and numerical study on the mitigation of autogenous shrinkage of cementitious material

Autogenous deformation and coefficient of thermal expansion of early-age concrete: Initial outcomes of a study using a newly-developed Temperature Stress Testing Machine

EXPERIMENTAL INVESTIGATION ON CONCRETE PERFORATED BRICK WALL SHINKAGE AT DIFFERENT AGES

Improvement of Autogenous Shrinkage Measurement for Cement Paste at Very Early Age: Corrugated Tube Method Using Non-Contact Sensors

Experimental Investigation of the Deformational Behavior of the Interfacial Transition Zone (itz) in Concrete During Freezing and Thawing Cycles

Incorporating elastic and creep deformations in modelling the three-dimensional autogenous shrinkage of cement paste

Study on Effects of Artificial Short Cracks of Roller Compacted Concrete Gravity Dam(RCCD)

Autogenous shrinkage of shrinkage-compensating concrete

Experimental study of RCC mixed with magnesia

Integrative Study on the Effect of Internal Curing on Autogenous and Drying Shrinkage of High-Strength Concrete

Influences of Water-binder Ratio and Dosage of Fly Ash on Autogeneous Shrinkage of Shrinkage-Compensating Concrete

A Prediction Model for Autogenous Shrinkage of High-Performance Concrete in Bridge Engineering

Numerical study of the autogenous shrinkage of cement pastes with supplementary cementitious materials based on solidification theory

Influence of Specimen Size on Autogenous Volume Deformation of Long-Aged MgO-Admixed Concrete

Effect of Working Temperature Conditions on the Autogenous Deformation of High-Performance Concrete Mixed with MgO Expansive Agent

Early-age Autogenous Shrinkage and Stress Characteristics of High-Performance Concrete at the Mesoscopic Level

Decoupling of Autogenous Shrinkage and Tensile Creep Strain in High Strength Concrete at Early Ages

Clarifying the Deformation Restriction of Unhydrated Phase in Cement Paste to Its Autogenous Shrinkage