Abstract:High -strength concrete (HSC) suffers severe shrinkage, which deteriorates the structural safety of buildings over time. Therefore, this study aims to search for indexes that could reflect the development of early drying shrinkage in HSC with different types/quantities of minerals. The influences of minerals on the internal pore structure and water evaporation of HSC were investigated by experimental work, whose correlation with early drying shrinkage was clarified. The results indicated that pore size distribution (PSD) and water evaporation of HSC should be taken into account simultaneously, facilitating the proposal of a two -factor parameter, rs, and a smaller rs was accompanied by greater drying shrinkage of samples. In addition, only partial mesopore lost water that led to drying shrinkage of HSC instead of water in all mesopores. Finally, an early drying shrinkage model of HSC based on rs was established correspondingly, which was in line with the experimental data, showing great accuracy, suitability and values in practice in reflecting early drying shrinkage behaviors of the HSC selected in this study. However, the current model is based on pore structure parameters obtained from mercury intrusion porosimetry (MIP). The backscattered electron image analysis (BSE-IA) measurement of pore structure indicates that MIP underestimates the content of pores larger than 200 nm. Therefore, the actual parameter rs should be greater than the currently calculated value. In the future, with the development of pore structure testing techniques, a more accurate rs value that closely represents the true value should be obtained, and a more universal model that considers several factors should be established.

Micromechanical Modeling on Autogenous and Drying Shrinkages of Concrete

Identification of Indexes That Could Reflect Early Drying Shrinkage of High Strength Concrete with Minerals

Integrative Studies on Autogenous and Drying Shrinkages of Concrete at Early-Age

Experimental and Theoretical Studies on Autogenous Shrinkage of Concrete at Early Ages

Is Early Drying Shrinkage Still Determined by the Mesopore Content? A Case Study of Cement Paste with Minerals

Shrinkage And Interior Humidity Of Concrete Under Dry-Wet Cycles

Numerical Analysis of Drying Shrinkage in Long Reinforced Concrete Structure

Modeling on Shrinkage Stress in Early-Age Concrete Pavements

Moisture Movement in Early-Age Concrete under Cement Hydration and Environmental Drying

Tests and Simulations of Interior Humidity and Shrinkage of Concrete under Sealed Condition

Computational Modeling of Drying Shrinkage in Early‐Age Concrete

Shrinkage Stress in Concrete under Dry–wet Cycles: an Example with Concrete Column

Calculation of shrinkage strain in early-age concrete structures---an example with concrete pavements

A Coupled Hygro-Thermal Model of Early-Age Concrete Based on Micro-Pore Structure Evolution

Evaluation of shrinkage induced cracking in early age concrete: From ring test to circular column

Calculation of Moisture Distribution in Early-Age Concrete

Theoretical Modeling and Verification of Concrete Moisture Diffusion Surface Factor

A Mesoscale Three-Dimensional Moisture Transport Model in Concrete

Calculation of Shrinkage Stress in Concrete Structures with Impact of Internal Curing

Modelling of Coupled Shrinkage and Creep in Multiphase Formulations for Hardening Concrete

Early-age Autogenous Shrinkage and Stress Characteristics of High-Performance Concrete at the Mesoscopic Level