Abstract:This study proposed to introduce a combination of crushed granite (CG), superabsorbent polymer (SAP), and expansive agent (EA) into ultrahigh-performance concrete (UHPC) to mitigate the early autogenous shrinkage of UHPC without causing deterioration of its workability and mechanical performance. To this end, the effects of CG, SAP, and EA individually and their combinations on the workability, compressive strength, and autogenous shrinkage of UHPC were investigated. The results showed that CG, EA, and SAP all reduced the autogenous shrinkage of UHPC. However, the addition of CG and EA deteriorated the workability of UHPC, while the introduction of SAP decreased the compressive strength of UHPC. When CG (14.7% vol.), 1% EA, and 0.15% SAP were combined (CG+EA-1+SAP-0.15), UHPC showed the best overall performance. Specifically, the 7-day autogenous shrinkage of the CG+EA-1+SAP-0.15 group was 296.1 με, which was 68% lower than the reference group (without CG, EA, and SAP); the 28-day compressive strength was slightly improved; and the slump flow was only 1.6% lower than that of the reference group, which was negligible. The results of thermogravimetry analysis showed that SAP could enhance the hydration of portland cement and EA, and could also promote the pozzolanic reaction of ground granulated blast furnace slag and silica fume. The results of mercury intrusion porosimetry demonstrated that the microstructure of UHPC was refined due to the enhancement of hydration by internal curing of SAP. Besides, when CG, EA, and SAP were combined, the total porosity of UHPCs first decreased and then increased when the dosage of SAP increased. Specifically, the total porosities of the reference, CG+EA-1+SAP-0.1, CG+EA-1+SAP-0.15, and CG+EA-1+SAP-0.2 groups were 9.6%, 9.2%, 5.5%, and 9.4%, respectively. The CG+EA-1+SAP-0.15 group had minimum porosity, which was 42.87% lower than reference group. The above results demonstrated that the combined use of CG, SAP, and EA can effectively mitigate the early autogenous shrinkage of UHPC, but the optimal ratio between EA and SAP should be further studied.

Effects of Shrinkage Reducing Agent and Expansive Admixture on the Volume Deformation of Ultrahigh Performance Concrete

Powder Gradation Effect on the Fresh, Mechanical, and Early-Age Shrinkage Properties of UHPC

Effect of Crushed Granite, Superabsorbent Polymer, and Expansive Agent on the Workability, Compressive Properties, and Autogenous Shrinkage of Ultrahigh-Performance Concrete

Effects of Shrinkage Reducing Agent and Expanded Cement on UHPC Fluidity, Mechanical Properties, and Shrinkage Performance

Investigation of early drying shrinkage of ultrahigh-performance concrete under windy conditions

Solving shrinkage problem of ultra-high-performance concrete by a combined use of expansive agent, super absorbent polymer, and shrinkage-reducing agent

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

Impact of High-Performance Expansion and Shrinkage-Reducing Agents on the Mechanical Properties and Shrinkage Compensation of High-Strength Concrete

Shrinkage Mitigation of an Ultra-High Performance Concrete Submitted to Various Mixing and Curing Conditions

Influence of Superplasticiser on Early Shrinkage and Total Shrinkage of Concrete

Humidity Sensitivity of Hydration of Expansive Agent and Its Expansive Efficiency in Ultra-High Performance Concrete

Synergetic Effect of Superabsorbent Polymer and CaO-Based Expansive Agent on Mitigating Autogenous Shrinkage of UHPC Matrix

Autogenous shrinkage prediction models and microstructure of UHPC with single or binary addition of an expansive agent and steel fibers

Plastic and early-age shrinkage of ultra-high performance concrete (UHPC): Experimental study of the effect of water to binder ratios, silica fume dosages under controlled curing conditions

Mitigation on the autogenous shrinkage of ultra-high performance concrete via using MgO expansive agent

Mechanical Properties and Shrinkage of Ultrahigh-Performance Concrete Containing Lithium Carbonate and Nano-Calcium Carbonate

Effects of Steel Slag Powder and Expansive Agent on the Properties of Ultra-High Performance Concrete (UHPC): Based on a Case Study

Effects of Type and Content of Fibers, Water-to-Cement Ratio, and Cementitious Materials on the Shrinkage and Creep of Ultra-High Performance Concrete

Engineering Performance and Expansion Mechanism of MgO Expansion Agent in Ultra-High Performance Concrete (UHPC)

Mechanical Performance and Microstructure of Ultra-High-Performance Concrete Modified by Calcium Sulfoaluminate Cement

Research on shrinkage control technology of lightweight ultra-high performance concrete