Research on shrinkage control technology of lightweight ultra-high performance concrete

J. Fu,Z.S. Wang,Y.B. Min,Q.J. Ding

DOI: https://doi.org/10.1201/9781003251125-7

2021-11-25

Abstract:Relying on the Wanzhou Xintian Yangtze River Bridge project and taking the amount of fiber and whether the specimen is sealed or not as the changing parameters, the shrinkage of light weight ultra-high performance concrete (LUHPC) was studied. The results show that as the volume ratio of steel fiber increases, the shrinkage of LUHPC gradually decreases. As the amount of expansion agent increases, the shrinkage of LUHPC decreases, and the effect of incorporating high pedormance calcium sulpho aluminate(HCSA) expansion agent with calcium sulfo aluminate and calcium oxide as dual expansion sources is better. Covering with plastic film at an early age to retain water has a beneficial effect on inhibiting concrete shrinkage, and its shrinkage is 44.9% less than the blank control group. Furthermore, the internal curing effect of the pre-wet fine light aggregate can significantly alleviate the “water competition” between the expansion agent and the gelling material, and give full play to the expansion effect of the expansion agent, which significantly reduce the shrinkage of LUHPC.