Mechanical properties and microstructure of ultra-high strength concrete with lightweight aggregate
Lingqi Meng,Chunxiao Zhang,Jiuqi Wei,Lei Li,Jingbiao Liu,Shihe Wang,Yahong Ding
DOI: https://doi.org/10.1016/j.cscm.2022.e01745
IF: 4.934
2022-12-10
Case Studies in Construction Materials
Abstract:In recent years, the development of concrete has been toward to the direction of lightweight and high strengthening. This study developed a kind of lightweight ultra-high strength concrete(L-UHSC) through the comprehensive design method, which had an apparent density rang of 1995kg/m 3 -2114kg/m 3 and a compressive strength of 102.4 MPa-114.5 MPa. The specific strength of the designed L-UHSC is more than 50 MPa/(t/m 3 ), which is higher than ordinary structural lightweight aggregate concrete (LAC). Additionally, the roles of high-performance paste, lightweight aggregate (LWA) and steel fiber in L-UHSC were revealed through scanning electron microscopy (SEM), mercury intrusion porosimetry (MIP) and strength test. The findings revealed that SF content, rather than the binder-sand ratio and aggregate ratio, has a greater impact on density and strength, and the aggregate ratio having the least effect. As steel fiber content increases from 0.5% to 2.0%, compressive strength, flexural strength and splitting tensile strength of LAC increase by 44.3%, 120% and 151%, respectively, which is higher than that of ultra-high performance (UHPC). The micromorphology and pore structure research suggested that the high-performance paste plays a keystone role in achieving the ultra-high strength, and LWAs mainly affected strength through improving pore structure. In addition, small size pre-wetted LWA is more conducive to concrete strength. Our preliminary results provide a reference for the research and development of lightweight ultra-high strength cement composites.
construction & building technology,materials science, multidisciplinary,engineering, civil