Abstract:ABSTRACT In this article, we report an acrylate‐based three‐dimensional (3D) printing stereolithography rapid‐prototyping photosensitive resin with a low viscosity, small volumetric shrinkage, high photoreactivity, and excellent strength. The resin was a compound prepared with bisphenol A epoxy acrylate (BAEA) as the main matrix, 1,6‐hexanediol diacrylate (HDDA) and tri(propylene glycol) diacrylate (TPGDA) as reactive diluents, pentaerythritol triacrylate (PETA) as the crosslinking agent, and 2‐hydroxy‐2‐methyl propiophenone (1173) and diphenyl(2,4,6‐trimethyl benzoyl)phosphine oxide (TPO) as photoinitiators. The photocuring kinetics of the resins with different photoinitiator types and loadings were studied via real‐time IR spectroscopy, which provided insights into the optimization of photoinitiator composition and printing parameter settings. The results show that the content change of each component affected the viscosity of the photosensitive resin; this was accompanied by fluctuations in the volume shrinkage and mechanical strength of the cured products. Although an increase in the molar ratio of the reactive diluent remarkably reduced the viscosity of the photosensitive resin and thereby boosted photopolymerization, it also caused an increase in the volume shrinkage and a sacrifice of mechanical strength. Finally, as shown by a comparison of the other samples we studied, the resin composed of 30 mmol HDDA, 50 mmol TPGDA, 10 mmol PETA, 10 mmol BAEA, 2.5 mol % TPO, and 2.5 mol % 1173 achieved the best viscosity of 239.53 mPa s at 25 °C, the minimum shrinkage rate of 4.36%, and the maximum tensile strength of 43.19 MPa. The 3D printing curing products had the closest size to the design dimensions of the computer‐aided design model; this indicated that the resin seemed to be a most promising candidate for 3D printing applications. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136 , 47487.

Research on a Low Curl Photocurable Resin for Stereolithography

Development of a Hybrid Photopolymer for Stereolithography

Study on the Effect of Photocuring Resin Shrinkage on Parts Curl Distortion in the Process of Laser Rapid Prototyping

Preparation of a Novel Cationic Photosensitive Resin (3D-SLR01) for Stereolithography 3D Printing and Determination of Its Some Properties

Research Progress of Rapid Prototyping and Photocurable Resin

Shrinkage Effects in Photopolymerizable Resin containing Polymer Filler for SL

A Comparative Study on 3D Printed Silicone-Epoxy/acrylate Hybrid Polymers Via Pure Photopolymerization and Dual-Curing Mechanisms

Low Adhesion Continuous Constrained-Surface Projection Stereolithography Process Based on Curing Degree Control

STUDY ON THE UV-CURING OF A NEW ALICYCLIC EPOXY ACRYLATE RESIN

Silicone–Epoxy‐Based Hybrid Photopolymers for 3D Printing

Preparation and Study of Stereolithography Photosensitive Resin Based on 405 Nm Uv Light Source

Acrylate-based photosensitive resin for stereolithographic three-dimensional printing

Study on Free-Radical Resins Used in Stereolithography

Aliphatic silicone‐epoxy based hybrid photopolymers applied in stereolithography 3D printing

Highly stretchable dual‐cure photosensitive resin for digital light processing printing

Research on the Resolution of Micro Stereo Lithography

Preparation withthe photosensitive resin for 3D printing stereolithography technique and study on its properties

Preparation and Application of Photocuring Resin

A Cross-Linking Strategy with Moderated Pre-Polymerization of Resin for Stereolithography

Evaluation of Thiol-Ene Photo-Curable Resins Using in Rapid Prototyping

Continuous 3D Printing by Controlling the Curing Degree of Hybrid UV Curing Resin Polymer