Abstract:The structure and surface acidity of zirconia-supported tungsten oxide are studied by using BET, XRD, FT Raman, Tian–Calvet microcalorimetry as well as XPS. Three different crystal forms of ZrO 2 and their hydroxide precursors were prepared in a controllable way. It was found that the starting material and preparing conditions used have a significant effect on the structure of ZrO 2 obtained. The tungstate species on zirconium hydroxide generally promote the transformation of the hydroxide precursor into tetragonal ZrO 2 , while the same species on the pre-calcined ZrO 2 has less effect during calcination. A bulk-phase WO 3 existed in the samples prepared by initially impregnating the monoclinic, tetragonal and cubic ZrO 2 or the hydroxide precursors of m- and t-ZrO 2 , while no crystalline WO 3 was present in the samples prepared by initially impregnating the hydroxide precursor of c-ZrO 2 . Raman results revealed that the surface tungstate(s) on three different zirconium hydroxides or their respective zirconia have similar structural features before calcination. The surface tungsten oxides and some WO 3 bulk phase are the detectable tungsten species in the final samples, the ratio of each component is strongly dependent on the preparation history and the nature of the support. Creation of very strong acidic sites on the zirconia-supported tungsten oxide is related to the crystal form of zirconia itself, the type of tungsten oxide species, and the cooperation between the surface tungsten oxide overlayer and zirconia. The strong acidic sites can be completely poisoned by the remaining sodium ion impurities, but have not been appreciably influenced by added yttrium component. The crystalline WO 3 seems of little importance in building up the strong surface acidity.

Dispersion and Interaction State of Boria on Zirconia Surface

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

The Texture,Structure and Surface Acidity of B_2O_3/ZrO_2 Solid Acid Catalyst Calcined at 700℃

Effect of Supported Na+Ions on the Texture Properties of ZrO2

Pressureless Sintering of Zirconium Diboride Ceramics with Boron Additive

Oxygen Contamination on the Surface of Zrb2 Powders and Its Removal

Synthesis of Ultra-Fine and High-Pure Zirconium Diboride Powders Using Solution-Based Processing

Effect of dispersants on the physicochemical properties of ultra-fine ZrB2 powder in Sol-gel synthesis

PREPARATION AND INTERFACE ANALYSIS OF ZrB2/Al2O3 COMPOSITE POWDERS

Dispersion States and Br(?)nsted Acidity Feature of Nb_2O_5 on t-ZrO_2

The Incorporated Dispersion of Vanadium Oxide and Its Influence on the Textural Properties of Tetragonal Zro2

Structure Characterization and Monolayer Dispersion Phenomenon of MgO-ZrO2 Prepared by Co-precipitation

Carbothermal Reduction Synthesis Of Zirconium Diboride Powders Assisted By Microwave

IR and Raman investigation on the structure of (100-x)B2O3-x[0.5 BaO–0.5 ZnO] glasses

Influence of dispersion method of LaF3 in ZrB2-based ceramics on high-temperature oxidation resistance

Dispersion States and Bronsted Acidity Feature of Nb(2)O(5)on t-ZrO2

Dispersion behavior of zirconia nanocrystals and their surface functionalization with vinyl group-containing ligands.

Dispersion of Potassium Nitrate and the Resulting Strong Basicity on Zirconia

The structure and surface acidity of zirconia-supported tungsten oxides

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Dispersion states and brønsted acidity feature of Nb 2O 5on t-ZrO 2