Abstract:In this paper, we report a simple melt impregnation method by using cheap mesophase pitches (MPs) as carbon precursors to prepare ordered mesoporous carbon with ordered graphitized pore walls at low temperature. This facile procedure includes melting MPs at 140 degreesC and impregnation of the melt into hexagonal or bicontinuous cubic mesoporous silica templates. After the removal of silica templates by HF solution, ordered mesoporous carbon materials with replica structures of 2-D hexagonal p6mm or cubic Ia (3) over bard symmetry were derived. The pore walls of the hexagonal mesoporous carbon products are composed of graphitized domains with the (002) crystallographic plane of the graphite perpendicular to the long axis of the carbon nanorods. Theoretical computations show that negatively charged O atoms of Si-OH and Si-O-Si from the surface of mesoporous silica channels can interact with the positive charged H atoms of the MPs, which makes the stacking units incorporate into the pores with the (002) plane vertical to the channels, and finally the oriented periodicity of the graphite domains is formed. N(2) sorption measurements show that the materials possess no micropores. For the bicontinuous cubic mesoporous carbon, HRTEM images show that the material is a true replica framework of la3 ($) over bard symmetry. The graphitized structure of the pore walls seems to have an orientation related to the bicontinuous pore structure, which could not be simply defined based on current TEM results. Graphitized carbon nanofiber bundles with a uniform diameter of about 7 nm were obtained by using Fe(2)O(3) nanoparticle doped mesoporous silica as a template. A spiral graphite structure was observed for the materials. Cyclic voltammetry measurements show low charge/discharge currents for the graphitized materials compared to the amorphous mesoporous carbon, further confirming the anisotropic character of the graphitized mesoporous carbons. The method can be widely applied to the hard-templating synthesis of graphitized carbon nanostructures and other doped carbon nanomaterials.

STUDY ON MECHANISM OF MESOPORE FORMATION OF PITCH-BASED SPHERICAL ACTIVATED CARBON USING IRON AS CATALYST

Effects of Pore Structure on Methanol Selectivity in Carbon Monoxide Hydrogenation

AN INVESTIGATION ON MESOPORE EVOLUTION MECHANISM OF ACTIVATED CARBON SPHERES BY EXAMINING THE CHANGE OF IRON STATE

Examining the change of iron state

Characteristic and Mechanistic Study of Enhanced Carbon-Based Synfuel from Biomass and Coal by Magnetite Additive for Synergistic Co-Carbonization Technology.

Wetting and Spreading Behavior of Molten Iron in Contact with Graphite Substrate: Interfacial Effects

Insight into pore structures evolution and applications in lithium-sulfur battery of pitch fractions-based activated carbons

Insight into the Pyrolysis Behaviors of Petroleum-Driven Mesophase Pitch via ReaxFF Molecular Dynamics and In Situ TG-FTIR/MS

Mesophase formation of coal-tar pitches used for impregnant of C/C composites

A study on the preparation of pitch-based high-strength columnar activated carbon and mechanism of phenol adsorption from aqueous solution

Homogeneous-pore-creation in pitch-based carbon fibers by extraction-activation and their application as supports for catalytic hydrogenation

Petroleum Pitch-Derived Porous Carbon Materials as Metal-Free Catalyst for Dry Reforming of Methane

A Simple Melt Impregnation Method to Synthesize Ordered Mesoporous Carbon and Carbon Nanofiber Bundles with Graphitized Structure from Pitches

Genesis of an Fe5C2@Fe3O4 core/shell structure during CO carburization of metallic iron nanoparticles

Preparation and characterization of pitch coke from oxidized polymerized pitch

Preparation of Activated Carbon Microspheres from Phenolic Resin with Metal Compounds by Sub- and Supercritical Water Activation

Preparation and Characterization of Mesocarbon Microbeads by the Co-Polycondensation of High-Temperature Coal Tar Pitch and Coal Pyrolytic Extracts

Tuning the carbon morphology by pyrolysis in AlCl3–NaCl molten salt from coal tar pitch

Preparation of Mesophase Pitch with Fine-Flow Texture from Ethylene Tar/Naphthalene by Catalytic Synthesis for High-Thermal-Conductivity Carbon Fibers

Synthesis, characterization and adsorption capacity of magnetic carbon composites activated by CO2: implication for the catalytic mechanisms of iron salts

Realizing of ZSM-5 microspheres with enhanced catalytic properties prepared from iron ore tailings via solid-phase conversion method