Abstract:Resistive, magnetoresistive and magnetic properties of four kinds of pressed CrO2 powders, synthesized by hydrothermal method of chromic anhydride have been investigated. The particles in powders constituted of rounded particles (diameter 120 nm) or needle-shaped crystals with an average diameter of 22.9 nm and average length of 302 nm. All of the particles had a surface dielectric shell of varying thickness and different types (such as oxyhydroxide -CrOOH or chromium oxide Cr2O3). For all the samples at low temperatures we found non-metallic temperature dependence of resistivity and giant negative magnetoresistance (MR). The maximum value of MR at low temperatures (T \approx 5 K) is \approx 37% in relatively small fields (0.5 T). At higher temperatures there was a rapid decrease of MR (up to \approx 1% / T at T \approx 200 K). The main objective of this work was studying the influence of properties and thickness of the intergranular dielectric layers, as well as CrO2 particle shape, on the magnitude of the tunneling resistance and MR of the pressed powder. The new results obtained in this study include: (1) detection at low temperatures in powders with needle-like particles a new type of MR hysteresis, and nonmonotonic MR behaviour with increasing magnetic field (absolute value of the MR at first grows rather rapidly with the field, and then begins diminishing markedly, forming a maximum), and (2) detection of non-monotonic temperature dependence, where - a field in which the resistance in a magnetic field has a maximum, as well as finding discrepancies in values of and coercivity fields, (3) detection of the anisotropy of MR, depending on the relative orientation of the transport current and the magnetic field, (4) a new method of synthesis, to regulate the thickness of dielectric coating.

Characterization of the Natural Barriers of Intergranular Tunnel Junctions: Cr2O3 Surface Layers on CrO2 Nanoparticles

Interfacial Composition and Microstructure of Fe3o4 Magnetic Tunnel Junctions

Features of Low Temperature Tunnel Magnetoresistance in Pressed Powder of Chromium Dioxide

Resistive and magnetoresistive properties of CrO2 pressed powders with different types of inter-granular dielectric layers

Spin-dependent Tunneling Transport into CrO2 Nanorod Devices with Nonmagnetic Contacts.

High magnetoresistance performance of epitaxial half-metallic CrO 2 -based magnetic junctions

Probing magnetism in 2D van der Waals crystalline insulators via electron tunneling

X-Ray Observations of V4641 SGR (= SAX J1819.3-2525) During the Brief and Violent Outburst of 2003

Thermal Characterization of Ultrathin MgO Tunnel Barriers

Difference between chemical structures of the interface at the Al-oxide tunneling barrier prepared by plasma or by radical oxidation

Intermixing of iron and cobalt with oxygen-rich magnesium oxide in CoFeB/MgO/CoFeB magnetic tunneling junctions

Dependence of Giant Tunnel Magnetoresistance of Sputtered CoFeB/MgO/CoFeB Magnetic Tunnel Junctions on MgO Barrier Thickness and Annealing Temperatur

Thermal Stability of Ir-Mn∕Co-Fe-B∕Al-O∕Co-Fe-B Tunnel Junctions

Scaling Behavior of Magnetoresistance with the Layer Number in CrI3 Magnetic Tunnel Junctions

Tunneling Magnetoresistance Effect in Co/TPD Granular Films

Magnetoresistance in Arrays of Fine Graphite Powders with Nearest-Neighbor Tunneling Conduction

Observation of the Barrier Structure in Magnetic Tunnel Junctions Using High-Resolution Electron Microscopy and Electron Holography

Thermal and Electrical Stability Behavior of a Magnetic Tunnel Junction With a New Zr-Alloyed Al-Oxide Barrier

Hole transport across MgO-based magnetic tunnel junctions with high resistance-area product due to oxygen vacancies

Annealing Effect of Magnetic Tunnel Junctions with One Feox Layer Inserted at the Al2o3/Cofe Interface

Influence of chemical and magnetic interface properties of Co-Fe-B / MgO / Co-Fe-B tunnel junctions on the annealing temperature dependence of the magnetoresistance