Interrupted Oxidation Kinetics of the Tial Alloys in Static Air

HL Qu,L Zhou,HR Wei

DOI: https://doi.org/10.3321/j.issn:1002-185x.2000.01.003

2000-01-01

Rare Metal Materials and Engineering

Abstract:The interrupted oxidation behaviours of five kinds of as-cast TIAl alloys at 700 degrees C similar to 1 000 degrees C in static air have been investigated using thermogravimetric analysis (TGA). The results show that the oxidation of the TiAl alloys at 700 degrees C for 100 h is slight, and the interrupted oxidation kinetic curves of the TiAl alloys at 800 degrees C similar to 1 000 degrees C for 100 h can be described by a power function (Delta M-n=k(n)t, where 1 less than or equal to n less than or equal to 2 normally), indicating that the interrupted oxidation curves of the TiAl alloys lie in between linear and parabolic ones. Alloying constituents of the TiAl alloys remarkably influence the oxidation behaviour at middle and high temperatures (for example 900 C), while the differences between the oxidation behaviours of the five TiAl-based alloys studied become smaller as the oxidizing temperature increases further (for example up to 1 000 degrees C). The oxidation resistance of binary TiAl alloys is better than that of ternary TiAl-Cr alloys. The oxide layers spall off when TiAl alloys oxidize at high temperature or for long times, thereby causing the oxidation to accelerate.