Abstract:Mesoporous carbon materials with ultra-thin carbon pore walls and highly dispersed Ni nanoparticles have been successfully prepared by using two different SBA-15 silicas as hard templates and 2,3-dihydroxynaphthalene (DHN) as a carbon precursor. The nickel precursor was a concentrated nickel nitrate hexahydrate [Ni(NO3)(2)center dot 6H(2)O] solution in 2-propanol, which was added to the carbon-silica nanocomposite prior to thermal treatment. The samples studied were analyzed by thermogravimetry (TG), nitrogen adsorption at -196 degrees C, powder X-ray diffraction (XRD), Raman spectroscopy, scanning and transmission electron microscopy (STEM), and in situ electron diffraction X-ray spectroscopy (EDX). While TG analysis revealed carbon contents lower than 30 wt.-%, nitrogen adsorption provided information about the homogeneity of the carbon thin film deposited onto the mesopore walls of the ordered silica templates SBA-15. The templates, carbon-silica nanocomposites, and carbon inverse replicas with nickel nanoparticles exhibit uniform pores, high surface areas, and large pore volumes. Partially graphitic carbon was identified by the presence of a characteristic G band in the Raman spectra, whereas the diffraction peak attributed to the stacking of graphene planes was not observed by powder XRD. The presence of ordered domains in the carbon materials studied was confirmed by small angle XRD and STEM imaging. In addition, the STEM images revealed that the nickel nanoparticles are uniform in size, ca. 3 nm, and are homogeneously dispersed on the tubular carbon walls. A few larger clusters of nickel, ca. 60 nm, present on the external surface, were identified by powder XRD as metallic Ni. The in situ EDX revealed that the small nanoparticles are largely composed of Ni with traces of NiO. Similar nanoparticle dispersions have been reported only for Ni-containing multiwalled carbon nanotubes (CNTs), whereas previously reported ordered mesoporous carbon materials, CMK-3, possess larger Ni/NiO nanoparticles. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2009)

Preparation and corresponding structure of nickel foam

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Relationship Between Tensile Strength and Preparation Conditions for Nickel Foam

Preparation of hexagonal close-packed nickel nanoparticles via a thermal decomposition approach using nickel acetate tetrahydrate as a precursor

Facile Synthesis of Nickel Nanofoam Architectures for Applications in Li‐Ion Batteries

Preparation of Hollow Nickel Fibres by Electroless-Plating Technique

Mesoporous Carbon Materials with Ultra‐Thin Pore Walls and Highly Dispersed Nickel Nanoparticles

Sol-gel synthesis and characterization of foamed Ni 3 Pt alloys

Ton-scale preparation of single-crystal Ni-rich ternary cathode materials for high-performance lithium ion batteries

Three-Dimensional Interconnected Nickel Phosphide Networks with Hollow Microstructures and Desulfurization Performance

Scalable Production of Carbon Encapsulated Ni Nanoparticles by Water Arc Discharge: Structural and Magnetic Properties

Conformation and Microstructure of Carbon Nanofibers Deposited on Foam Ni

Synthesis and Characterization of Graphite Nanofibers Deposited on Nickel Foams

Lattice-matching Ni-based scaffold with a spongy cover for uniform electric field against lithium dendrites

Study of Oxidation-Resistant NiCrAl–Al Coatings Co-Deposited by Electrophoresis on Nickel Foams

Preparation Of Nickel Foam Supported Fe2o3@Ni3s2 Nanowires Network Electrode And Electrocatalytic Oxygen Evolution Performance

Facile fabrication of novel high-performance electromagnetic interference shielding nickel foam

Electrochemical Performances of Nanostructured Ni3P–Ni Films Electrodeposited on Nickel Foam Substrate

Improving electrochemical performance of NiO films by electrodeposition on foam nickel substrates

Investigation of Tensile Properties and In Situ Analysis of Fracture Behavior in High-Porosity Open-Cell Nickel Foam

Preparation of Ultra-Fine Nickel by Electrochemical Milling Method