Abstract:Selective catalytic reduction (SCR) is a crucial technique for mitigating nitrogen oxides emission of internal combustion engines. Compared with vanadium-based catalysts, copper-based molecular sieve catalysts exhibit superior low-temperature catalytic performance and anti-aging properties. The catalytic characteristics of Cu-SSZ-13 catalyst in both fresh and aged states are investigated through experimental and numerical simulations. The catalytic performance of Cu-SSZ-13 catalyst with 200 g/L coating is investigated under wide inlet temperatures (180 °C–450 °C) and ANR (ammonia to nitrogen ratio) (1–1.4) conditions via an engine emission test device. Further, the apparatus is adopted to evaluate performance at various aging temperatures (600 °C, 700 °C, and 800 °C). The aging factor is introduced based on experimental results to establish and correct the kinetic model for SCR aging state. The results illuminate that the increase of ANR fails to compensate for decline of catalytic efficiency under low-temperature conditions (150 °C).The generated quantity of isocyanate acid through the side reaction of urea hydrolysis increases proportionally with ANR. And it increased supply only resulted in a marginal 1 %–3 % improvement of catalytic efficiency. As SV decreases from 60,000 h −1 to 35,000 h −1 , the catalyst efficiency increases from 22 % to 45 %, resulting in an elevation of reactant concentration and its gradient on the catalyst surface. This leads to accelerated reaction rates and enhanced diffusion effects. The catalytic efficiency can be significantly enhanced at low temperatures when NO 2 fraction in NOx falls within the range of 10 %–25 %. The sensitivity of SCR reactions to aging varies at low temperatures (<250 °C) due to the distinct reaction sites on catalyst for different types of SCR reactions. The NO 2 SCR reactions exhibit minimal susceptibility, while the rapid SCR reactions are significantly impeded. Moreover, it has been observed that the catalyst microstructure was completely deteriorated under hydrothermal aging test at 900 °C operating condition. In general, the low-temperature catalytic performance of Cu-SSZ-13 catalyst can be further optimized by pretreating inlet gas components and optimizing the catalyst structure.

Multi-stage Rapid Aging Mode for Durability Evaluation of Automotive Catalysts

Investigation of the Physicochemical Properties of Soot Subjected to Non-Catalytic and CeO2-catalytic Aging under Sequential Aerobic and Anaerobic Exhaust-Like Conditions Simulating the Transition from Engine Operation to Cessation

Experimental study on rapid aging test method of standard bench cycle (SBC) for three way catalytic converter

Accelerated aging for after-treatment devices of diesel engine: Method, emission characteristics, and equivalence

Thermal deactivation mechanism of the commercial Pt/Pd/Rh/CeO2-ZrO2/Al2O3 catalysts aged under different conditions for the aftertreatment of CNG-fueled vehicle exhaust

Experimental Study of Influence of Gasoline Fuel with MMT on Aging Performance of Three-Way Catalyst

Engine Accelerated Aging Method Developed to Study the Effect of Lubricant Formulations on Catalyzed Gasoline Particulate Filter Durability

Structure characterization of aged automobile exhaust catalysts using electron probe microanalysis

Aging of Commercial Diesel Oxidation Catalysts: A Preliminary Structure/Reactivity Study

Light‐Off Performance of Three‐Way Catalysts Before and After Accelerated Aging Test with Engine‐Dynamometer

Large-scale research on durability test cycle of fuel cell system based on CATC

An Experimental Study on the Effects of Gasoline with MMT on Aging Performance of Three-way Catalyst

Decelerating catalyst aging of natural gas engines using organic Rankine cycle under road conditions

Study of the Degradation Mechanisms of Carbon-Supported Platinum Fuel Cells Catalyst Via Different Accelerated Stress Test

Adaptability of M15 Methanol-Gasoline Blend to Catalysts

Study of durability of diesel vehicle emissions performance based on real driving emission measurement

Study on Three-Way Catalyst Deterioration Diagnosis Based on Oxygen Storage Rate Model

Experimental and numerical study of Cu-SSZ-13 SCR system for NOx reduction and hydrothermal aging under diesel exhaust conditions

Modeling of a DOC SCR-F SCR Exhaust Line for Design Optimization Taking Into Account Performance Degradation Due to Hydrothermal Aging

Aging Effects Observed in Automotive Fuel Cell Stacks by Applying a New Realistic Test Protocol and Humidity Control

Investigation of Performance Degradation and Control Strategies of PEMFC under Three Typical Operating Conditions