Abstract:VPO ultrafine particles were first successfully prepared by the supercritical fluid drying(SCFD). BET, XRD, TEM and XPS techniques were used to investigate the specific surface area, the phase composition, the grain size and the oxidation state of various samples. The VPO ultrafine particles after SCFD were activated in the reactant mixture or nitrogen at 673 K for 6 h. The results indicated that the obtained VPO ultrafine particles have a larger specific surface area, much smaller particle size and an unidentified crystalline phase in some cases after SCFD and activation. The kind and amount of promoter used and the activation atmosphere affect the physical properties of the VPO ultrafine particles. An ultrafine particle with Zr4+ and Mo6+ promoters, a surface area of 175. 6 m(2)/g and grain size of smaller 50 nm, can be obtained by activating in the nitrogen atmosphere at 673 K for 6 h, The oxidation state of surface vanadium atoms of ultrafine particles was around +4, similar to that of vanadium in (VO)(2)P2O7. The surface P/V molar ratio is in the range of 1. 04-1. 46, and is a little higher among the samples activated in N-2 atmosphere. Primary property evaluating results indicated that the small VPO particles showed very high selectivity but relatively low conversion.

The effect of preparation conditions on the structure and catalytic properties of VPO catalysts (1). Preparation and structure of catalysts

The effect of preparation conditions on the structure and catalytic properties of VPO catalysts: I. Preparation and structure of catalysts

The Effect of Preparation Conditions on the Structure and Catalytic Properties of VPO Catalysts: II. The Effect of Promoters on the Physical Properties of VPO Catalysts

Effects of Pore Structure on Methanol Selectivity in Carbon Monoxide Hydrogenation

Preparation of Vop Ultra-Fine Particles by Supercritical Fluid Drying

Influence of Preparation Conditions on Pore Structure and Activity of V2O5-WO3/TiO2 Honeycomb Catalysts

Preparation and Characterization of VPO Ultrafine Particles

EFFECT OF PREPARATION CONDITIONS ON THE PROPERTIES OF CoMoP HYDROTREATING CATALYST

The Effect of the Preparation Methods on the Structure of Wo3/Zro7

Effect of Preparation Condition on the Performance of MoVTeNbO Catalyst Materials for Selective Oxidation of Propane into Acrylic Acid

Effects of Ball Milling on the Doped Vanadium Phosphorus Oxide Catalysts

n-Butane oxidation over VPO catalysts supported on SBA-15

Kinetics and Optimization Studies of Modified VPO/-Al2O3 Catalyst Prepared in Situ for Cross-Aldol Condensation

Modulation Of Vanadium Phosphorous Oxide By Multi-Component Additives And Mechanical Milling

Novel Modifications in Preparing Vanadium Phosphorus Oxides and Their Applications for Partial Oxidation of N-Butane

Impact of Ultrasound Treatment Duration on Dihydrate Precursor Implying the Sesquihydrate Route

Effect of Preparation Parameters on Photoactivity of BiVO4 by Hydrothermal Method

VPO catalysts supported on H3PO4-treated ZrO2 highly active for n-butane oxidation

Effect of Preparation Methods on the Performance of Pt/TiO2 Catalysts for the Catalytic Oxidation of Carbon Monoxide in Simulated Sintering Flue Gas

Effects of alumina phases on the structure and performance of VOx/Al2O3 catalysts in non-oxidative propane dehydrogenation

Impact of Preparation Strategy on the Properties of Carbon-Supported Wacker-type Catalysts in Vapor-Phase Dimethyl Carbonate Synthesis