Abstract:F-V2O5-WO3/TiO2 catalysts were prepared by the impregnation method. As the content of F ions increased from 0.00 to 0.35 wt.%, the NO conversion of F-V2O5-WO3/TiO2 catalysts initially increased and then decreased. The 0.2F-V2O5-WO3/TiO2 catalyst (0.2 wt.% F ion) exhibited the best denitration (De-NOx) performance, with more than 95% NO conversion in the temperature range 160-360°C, and 99.0% N2 selectivity between 110 and 280°C. The addition of an appropriate amount of F ions eroded the surface morphology of the catalyst and reduced its grain size, thus enhancing the NO conversion at low temperature as well as the sulfur and water resistance of the V2O5-WO3/TiO2 catalyst. After selective catalytic reduction (SCR) reaction in a gas flow containing SO2 and H2O, the number of NH3 adsorption sites, active component content, specific surface area and pore volume decreased to different degrees. Ammonium sulfate species deposited on the catalyst surface, which blocked part of the active sites and reduced the NO conversion performance of the catalyst. On-line thermal regeneration could not completely recover the catalyst activity, although it prolonged the cumulative life of the catalyst. In addition, a mechanism for the effects of SO2 and H2O on catalyst NO conversion was proposed.

Influence of Preparation Conditions on Pore Structure and Activity of V2O5-WO3/TiO2 Honeycomb Catalysts

Effects of Pore Structure on Methanol Selectivity in Carbon Monoxide Hydrogenation

A Facile Route for Spraying Preparation of Pt/TiO2 Monolithic Catalysts Toward VOCs Combustion

Effect of preparation and reaction conditions on catalytic performances of honeycomb Pt/Al2O3

Monolith or Powder: Improper Sample Pretreatment May Mislead the Understanding of Industrial V2O5-WO3/TiO2 Catalysts Operated in Stationary Resources

Effects of Cordierite on V_2O_5-WO_3/TiO_2 Catalytic Performance

Effect of Preparation Methods on the Performance of Pt/TiO2 Catalysts for the Catalytic Oxidation of Carbon Monoxide in Simulated Sintering Flue Gas

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

The effect of preparation conditions on the structure and catalytic properties of VPO catalysts (1). Preparation and structure of catalysts

The effect of preparation conditions on the structure and catalytic properties of VPO catalysts: I. Preparation and structure of catalysts

Experimental Study on Preparation of V_2O_5-WO_3-MoO_3/TiO_2 Catalysts and Selective Reduction of NO_x with NH_3

Tungsten Oxide Modified V2O5-Sb2O3/TiO2 Monolithic Catalyst: NH3-SCR Activity and Sulfur Resistance

The Effect of Calcination Temperature on the Structure and Activity of TiO2/SiO2 Composite Catalysts Derived from Titanium Sulfate and Fly Ash Acid Sludge

The Progress of V<sub>2</sub>O<sub>5</sub>/TiO<sub>2</sub>-Based Catalyst in Hg<sup>0</sup> Removal and PCCD/Fs Decomposition

V<sub>2</sub>O<sub>5</sub>-WO<sub>3</sub>/TiO<sub>2</sub> Catalysts for Low Temperature NH<sub>3</sub> SCR: Catalytic Activity and Characterization

Performance of V_2O_5-WO_3-MoO_3/TiO_2 Catalyst for Selective Catalytic Reduction of NO_x by NH_3

V2O5-WO3/TiO2 Catalysts for Low Temperature NH3 SCR: Catalytic Activity and Characterization

[Effect of Vanadium and Tungsten Loadings on the Surface Characteristics and Catalytic Activities of V2O5-WO3/TiO2 Catalysts].

Effects of Preparation Parameters on the DeNOx Performance of V2O5/TiO2 Catalysts

Enhancement of SCR Activity and Mechanical Stability on Cordierite Supported V2O5-WO3/TiO2 Catalyst by Substrate Acid Pretreatment and Addition of Silica

Effects of SO2 and H2O on low-temperature NO conversion over F-V2O5-WO3/TiO2 catalysts