Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

Effects of Preparation Parameters on the DeNOx Performance of V2O5/TiO2 Catalysts

Effects of CrOx species doping on V2O5-WO3/TiO2 catalysts on selective catalytic reduction of NOx by NH3 at low temperature

Effects of H2O and SO2 on the Performance of V2O5/TiO2 Catalysts for Selective Catalytic Reduction of NO in Flue Gas

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Influence of WO3 Doping on Properties of V2O5/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx by NH3

Effect of SO2 Oxidation on SCR-DeNOx

Highly Efficient Mesoporous V2O5/WO3–TiO2 Catalyst for Selective Catalytic Reduction of NOx: Effect of the Valence of V on the Catalytic Performance

Experiment Study on SCR DeNOx Behavior of V2O5-WO3/TiO2 Catalysts

Selective catalytic reduction of NOx with NH3 over V2O5-WO3/TiO2-ZrO2 monolith catalysts

Effect of V2O5/WO3-TiO2 Catalyst Preparation Method on NOx Removal from Diesel Exhaust

Effect of pre-oxidation process on V2O5/AC catalyst for the selective catalytic reduction of NOx with NH3

Effect of Titanium Dioxide Support on the Properties for Selective Catalytic Reduction De-NO_x Catalyst

Effects of SO2 and H2O on low-temperature NO conversion over F-V2O5-WO3/TiO2 catalysts

The Properties and SCR De‐nox Application of Supported V2O5/TiO2 Catalysts with Different Polymerization State of VOx Species Controlled by the Ph Value of Their Precursors

Influence of texture structures of TiO2 supports on surface properties and SCR performance of V2 O5-MoO3/TiO2 catalyst

Effect of added SO2-4 on the performance of V2O5-based deNOx catalysts

Nano-TiO2 preparaed from different ways and application in SCR DeNOx catalyst

Study on DeNOx Performance of Honeycomb V_2O_5-WO_3/TiO_2 Catalysts

Study on the SCR Properties of Vanadium-based De-NOx Catalyst at Mid-low Temperature

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

Influence of WO3 doping on properties of V2O5/TiO2-SnO2catalysts for selective catalytic reduction of NOx by NH3