Abstract:In this study, the PEG-derived VPO precursors were subject to water refluxing (90 degrees C, 8 h) and in situ activation in a steam-containing environment. For comparison, the VPO precursors without water refluxing were also activated in a similar manner. The IR measurement indicated that the majority of PEG in the precursor has been removed during water refluxing, and the VPO is essentially unenwrapped by PEG. The consequence is an increase of particle size and crystallinity of VPO as well as decreases in surface acidity and site density. The activation of catalysts in a stream-containing environment has an influence on the content of V5+ species and on the reduction behavior of the VPO catalysts. The VPO catalyst activated with 20% water vapor (by volume) in the feed shows the highest crystallinity. Compared with the non-PEG-derived VPO precursor, the PEG-derived one undergoes structure changes of higher severity during the water/steam treatments. The VPO catalyst generated from the PEG-derived precursor with water refluxing and activated with steam (20%) exhibited a propane conversion of 25% and a (AA + HAc) selectivity of similar to 70%. The superior catalyst behavior can be interpreted in terms of the higher crystallinity of the (VO)(2)P2O7 phase, the lower content of V5+ species, and the milder surface acidity as caused by the water/steam treatments. (c) 2008 Elsevier B.V. All rights reserved.

Preparation of Vop Ultra-Fine Particles by Supercritical Fluid Drying

Preparation and Characterization of VPO Ultrafine Particles

The Effect of Preparation Conditions on the Structure and Catalytic Properties of VPO Catalysts: II. The Effect of Promoters on the Physical Properties of VPO Catalysts

The effect of preparation conditions on the structure and catalytic properties of VPO catalysts: I. Preparation and structure of catalysts

The effect of preparation conditions on the structure and catalytic properties of VPO catalysts (1). Preparation and structure of catalysts

Preparation of Metallic Monolithic Pt/FeCrAl Fiber Catalyst by Suspension Spraying for VOCs Combustion.

Solvent-free preparation of well-dispersed and highly active CrOx/VOx/TiO2-SiO2 bimetallic catalyst for bimodal UHMWPE/ HDPE in-reactor blends

Modulation Of Vanadium Phosphorous Oxide By Multi-Component Additives And Mechanical Milling

Effects of Ball Milling on the Doped Vanadium Phosphorus Oxide Catalysts

VPO catalysts supported on H3PO4-treated ZrO2 highly active for n-butane oxidation

Gas Phase Dehydration of Glycerol to Acrolein over Cs2.5H0.5PW12O40/Zr-MCM-41 Catalysts Prepared by Supercritical Impregnation

Surface active structure of ultra-fine Cu/ZrO2 catalysts used for the CO2+H2 to methanol reaction

Preparation of highly dispersed Pt–Sn/Al 2 O 3 catalysts via supercritical fluid deposition and their catalytic performance

Preparation of Fe-2(Moo4)(3) Ultrafine Particle Catalyst

Impact of Ultrasound Treatment Duration on Dihydrate Precursor Implying the Sesquihydrate Route

Synthesis of La modified ceria–zirconia solid solution by advanced supercritical ethanol drying technology and its application in Pd-only three-way catalyst

n-Butane oxidation over VPO catalysts supported on SBA-15

Water Modification of PEG-derived VPO for the Partial Oxidation of Propane

NOxRemoval over V2O5/WO3–TiO2Prepared by a Grinding Method: Influence of the Precursor on Vanadium Dispersion

Preparation and properties of ultrafine SO4 2- /ZrO2 superacid catalysts

Preparation and characterization of ultrafine particle CuO/ZrO2 catalysts I . Effect of hydrogel pH value on the morphology of the catalysts