Magnetostriction, Spin Reorientation and Mossbauer Study of Tb0.3Dy0.7(Fe1-xAlx)(1.95) Intermetallic Compounds
Xp Zheng,Ds Xue,Fs Li,Zh Cheng,Gh Wu,Bg Shen
DOI: https://doi.org/10.7498/aps.51.922
IF: 0.906
2002-01-01
Acta Physica Sinica
Abstract:The effect of Al substitution for Fe on the structure, magnetostriction, anisotropy and spin reorientation of a series Of Tb-0.3 Dy-0.7 (Fe1-xAlx)(1.95) alloys (x = 0, 0.05, 0.1, 0.15, 0.20, 0.25, 0.30, 0.35) at room temperature has been investigated. It was found that all the compositions of Tb-0.3 Dy-0.7 (Fe1-xAlx)(1.95) substantially retained the MgCu2-type C-15 cubic Laves phase structure and the lattice constant increases with increasing x. The substitution of Al increases slightly the magnetostriction in low magnetic field ( H less than or equal to 40kA.m(-1)) when x < 0.15, however, the magnetostriction decreases sharply, but is saturated more easily with increasing x in a higher applied field and the magnetostrictive effect disappears at x > 0.15. The intrinsic magnetostriction lambda(111) decreases sharply also with incresasing x. The Mossbauer spectra show that for 0 less than or equal to x < 0.15 alloys, spin reorientation is present with increasing Al concentration and the easy magnetization direction (EMD) undergoes the transition from [1 1 1] to [u v 0] and to [ u v w]. A small amount of non-magnetical phase exists for x = 0.15, and the alloys become paramagnetism when x > 0.15. The measurements of relative susceptibility indicate that the temperature of spin reorientation decreases with increasing x.