Abstract:A nanostructure of lithium-zinc copper ferrite (LiZnCu-Ferrite) prepared experimentally by the auto-combustion method depends on different parameters. The auto-combustion method operates at a temperature (160 °C) suitable for preparing the required nanostructure ferrite phase. The dependent composition was [Li0.5-xZnxCuxFe2.5-xO4 at (x = 0, 0.05, 0.15, 0.25, 0.35, and 0.45)]. A pre-firing at temperature (650 °C) was applied during the calcination process that was suitable to remove unwanted products. The sintering at temperature (800 °C) was suitable for a pelletized shape of ferrite samples. The X-ray diffraction (XRD) pattern showed a spinel structure of ferrite phase produced for all samples under study with the lattice constant in the range (8.345–8.368 Å) as a function of (x). The crystallite size was in the range (18.41–30.27 nm) calculated by the Scherrer method. The transmission electron microscope (TEM) showed a production of nanorods in the size range (10–45 nm) and nanoparticles in the size range (10–40 nm). There was a coincidence between the results of the XRD and TEM analyses. On the other hand, the scanning electron microscope (SEM) showed the surface morphology and the nature of grain size, which was a sign of the presence of nanostructure; it agreed with the XRD analysis. FTIR spectra showed evidence that the system Li0.5-xZnxCuxFe2.5-xO4 had spinal ferrite nanoparticles successfully prepared by sol-gel auto-combustion. A vibrating sample magnetometer (VSM) showed a change in magnetic parameters as compensation factor (x) increased for all composites of LiZnCu-ferrite such as saturation magnetization (Ms), initial magnetic permeability (μi), remanence (Mr), and coercive force (Hc) that measured from M − H loops. A saturation magnetization increased as a function of (x) and recorded a maximum value at (x = 0.15). While the coercivity, initial magnetic permeability (μi), and remanence magnetization enhanced as a function of (x) and recorded a maximum value at (x = 0.45).

Synthesis of Nanoparticles of Li Ferrite by Solid State Method

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Solid-state reaction synthesis of NiFe 2O 4 nanoparticles by optimizing the synthetic conditions

Synthesis and Characterization of Nickel Ferrite Nanoparticles Via Planetary Ball Milling Assisted Solid-State Reaction

Synthesis and Characterization of NiFe<sub>2</sub>O<sub>4</sub>Nanoparticles via Solid-State Reaction

Mechanochemical synthesis of nanocrystalline Ni-Zn ferrite

Synthesis And Characterization Of Nife2o4 Nanoparticles Via Solid-State Reaction

Solid State Synthesis of CoFe2O4 Nanoparticles at Low Heating Temperatures

Synthesis of CoFe2O4 Nanoparticles by a Low Temperature Microwave‐Assisted Ball‐Milling Technique

Solid-phase synthesis of nanophase alpha-Fe2O3 particle

Synthesis and Characterization of Ni0.7Zn0.3Fe2O4 and Mn0.7Zn0.3Fe2O4 Nanoparticles by Water-in-oil Microemulsion

Synthesis of Fe3O4 Nanoparticles by Co-precipitation and Micro-reactor Method

Processing Technology of Nano-sized Γ -Fe_2o_3 Particles by Solid-State Reaction

Research On Preparation And Characterization Of Nife2o4 Spinel Nanopowder Through Solid-State Reactions

Sol gel auto combustion method to prepare nanostructures LiZnCu ferrite

Mechanochemical Synthesis of Nanocrystalline Zinc Ferrite

Preparation and Magnetic Properties of Magnetite Nanoparticles by Sol–gel Method

Effect Of Nizn Ferrite Nanoparticles Upon The Structure And Magnetic And Gyromagnetic Properties Of Low-Temperature Processed Liznti Ferrites

Synthesis and Characterization of CoFe 2 O 4 Nanoparticles

Preparation of monodisperse ferrite nanocrystals with tunable morphology and magnetic properties.

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles