Solid State Synthesis of CoFe2O4 Nanoparticles at Low Heating Temperatures

Lei HUANG,Hai-bo WANG,JIAN-bo WANG,Qing-fang LIU,Wei-wei WANG

DOI: https://doi.org/10.3969/j.issn.1004-0366.2009.03.019

2009-01-01

Abstract:CoFe2O4 ferrite nanoparticles were synthesized by a method of solid state synthesis at low temperatures using CoCl2,FeCl3,NaOH as the materials.The structure,morphology,magnetic performance are characterized by a X-ray diffraction instrument(XRD),a scanning electron microscope(SEM)as well as a vibrating sample magnetometer(VSM).Mssbauer spectroscopy was used to analyse the samples.The results show that high purity of CoFe2O4 particles with the size distribution in the range from 11 to 56 nm can be obtained at low temperature(90℃).The single domain critical size is about 23 nm.Mssbauer spectra indicate that the hyperfine field of the samples increases as the annealing temperature rises.