Abstract:The influence of stress ratio ( R- ratio) and overload effect on the mixed mode fatigue crack growth (FCG) behaviour is experimentally assessed in this study. Mixed-mode FCG tests were conducted on EA4T steel, involving variations in R -ratios, overload types, and overload interval (OLI) cycle times. The results showed that the crack propagation prediction model, incorporating plasticity and roughness-induced crack closure effects as proposed in previous work based on the model of Christopher and Pokluda et al., outperforms four traditional models when fitting experimental data under different R- ratio conditions. Considering the impact of the R- ratio, the original mixed model was modified which shows an improvement of approximately 7 % in fitting experimental data. The ranking of overload retardation effects within overload types was as follows: single overload (SOL) > double overload (DOL) > multiple overload (MOL). The interval cycles incorporated within the overload sequence can weaken the crack closure effect caused by the crack tip overload. A smaller OLI can lead to the retardation effect of the preceding overload being overshadowed by the influence of the subsequent overload, thus diminishing the retardation effect. Increasing the OLI reduces interference among the retardation effects of different overloads, resulting in smaller interference zones for each overload retardation effect. The crack tip opening displacement was proposed as the delay parameter, and the rationality of the delay parameter was verified by combining it with the test data. The parameter effectively reflects the retardation state and aligns well with the test results

Effect of single overload on fatigue crack propagation rate for AISI 321 stainless steel under constant ΔK control

Effects of Tensile/compressive Overloads on Fatigue Crack Growth Behavior of an Extra-Low-interstitial Titanium Alloy

EFFECTS OF ENVIRONMENT ON THE OVERLOAD BEHAVIOR OF FATIGUE CRACK PROPAGATION FOR AISI 321 STAINLESS STEEL

DIC-based Studies of the Overloading Effects on the Fatigue Crack Propagation Behavior of Ti-6Al-4V ELI Alloy

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

STUDY OF FATIGUE CRACK GROWTH RETARDATION, CRACK TIP DEFORMATION AND CRACK CLOSURE UNDER SINGLE OVERLOAD APPLICATION FOR A537 STEEL

Effect of Initial Overload on the Low Cycle Fatigue Life of Gh4169 Alloy at Different Temperatures

Effect of overload occurence frequency on fatigue crack growth rate of steel A537

Instrumented indentation measurements of residual stresses around a crack tip under single tensile overloads

Effect of Single Overload on Fatigue Crack Growth in QSTE340TM Steel and Retardation Model Modification

Crack Growth Retardation of Single Overload for A537 Steel in a 3.5% NaCl Solution under Cathodic Potential and Free Corrosion Condition

Effect of single tensile overload on fatigue crack growth behavior of CP-Ti at negative load ratio

Retardation mechanisms and modeling of fatigue crack growth of a high-strength steel after single overload

EFFECT OF NON-PROPORTIONAL OVERLOADINGON FATIGUE CRACK GROWTH

Effect of stress ratio and overload on mixed-mode crack propagation behaviour of EA4T steel

Creep-fatigue interactive behavior and damage mechanism of TP321 stainless steel under hybrid-controlled conditions

Crack Tip Strain Evolution and Crack Closure During Overload of a Growing Fatigue Crack

The Retardation Effect of Combined Application of Stop-Hole and Overload on Sheet Steel

The Effect of Compression Loading on Fatigue Crack Propagation after a Single Tensile Overload at Negative Stress Ratios

Quantitative analysis of overload effect at crack tip on crack growth rate of 7005 aluminum alloy

Effect of Constant Cyclic Stress Coupling on the Fatigue Behavior of 304LN Stainless Steel