Metastable transformation and reordering of mult-phase Al3Ti-based intermetallics

Yunyi Fu,Gengxiang Hu,Wangyue Yang,Zuqing Sun
1999-01-01
Abstract:The disordering of multi-phase Al67Mn8Ti24Nb1 alloy during high-energy ball milling process and the heat induced reordering of the metastable powder were studied. During high-energy ball milling process the degree of order of the L12 structure matrix decreases to zero after 15h balling milling. The DO22 phase dissolved into the matrix, forming a disordered super-saturated fee solid solution. Further milling leds to the amorphous transition. So the sequence of structural evolution during ball milling is: L12+DO22 →L12 (weak ordering) →disordered fcc→fcc+amorphous→amorphous. The degree of order was determined using the 100/200 and 110/220 diffraction peaks. It is noted that the degree of order determined by 110/220 decreased more rapidly, which implies that the deformation occurred during milling, which results in some structural anisotropy. The heat induced reordering of the amorphous alloy has also been studied and the following structural transformation sequences were found: amorphous→disorder fcc→weakly ordered L12 with DO22 phase precipition→ordered L12 and completely precipitated DO22 second phase.
What problem does this paper attempt to address?