Abstract:Understanding the thermal stability of ceramic matrix composites is one of the necessary prerequisites for their engineering application. This study aimed to investigate the stress response and failure mechanism of SiC-coated Cf composite during thermal shock in an O2 free environment, at temperature between 500 and 1800 degrees C. Composites with a single layer of SiC coating, and a reinforcing phase are carbon fiber yarns with a threedimensional four-step braided structure. A meso-scale finite element model considering the orientation of fiber yarns was established to analyze thermal residual stress (TRS) and thermal shock stress (TSS) by transient analysis. Results indicated that the most dangerous position generated by the TRS was in the matrix close to the fiber yarn/matrix interface. Initial cracks first nucleated in the matrix, because the matrix was subjected to large residual compressive stress along the braiding direction, which is related to the distribution characteristics of the fiber yarns (braiding method). Fiber yarns with different orientation exhibited almost the same stress state, and interaction between fiber yarns resulted in a similar "twisted" state. For single fiber yarns, the principal axis and fiber yarn/fiber yarn interface were prone to failure. TSS in the composites rapidly increased during the initial cooling stage. A sudden change in temperature and stress gradient led to cracking and peeling at the composites/ coating interface. Possible failure modes and mechanisms of the composites with and without the SiC coating are discussed.

Analysis of Thermal Stresses in a Ceramic/Cemented Carbide Compact

Study on the Correlativity Between Grinding Parameters and Surface Residual Stresses in Ceramic

Finite Element Analysis of Thermal Stresses in Functionally Graded Cemented Carbides

Thermal Stress Analysis Of Functionally Graded Cemented Carbides

Residual Stresses Analysis of Diamond Coatings on Cemented Carbides

Theoretical Calculation and Numerical Simulation for Thermal Residual Stresses of Cemented Carbides

Finite Element Analysis of Thermal Residual Stress in Ceramic Functional Graded Material: Interface Optimization for Residual Reduction

FEM Analysis of the Stress Response and Failure Mechanism of SiC-coated Cf/ SiC Composites During Thermal Shock

Analytical modelling of thermal residual stresses and optimal design of ZrO2/(ZrO2+Ni) sandwich ceramics

Damage Evolution of the Interphase on C/SiC Composites with CZM Method

Stress Analysis for Cemented Carbides Under Different Loading Conditions Based on the Finite Element Method

Thermal Residual Stress Analysis of Diamond Coating on Graded Cemented Carbides

Residual Stress Estimation in Laminated ZrB2-SiC Ultra-High Temperature Ceramics with Strong Interfaces Using X-ray Diffraction and Indentation Techniques

Evaluation of Weak Interface Effect on the Residual Stresses in Layered SiC/TiC Composites by the Finite Element Method and X-Ray Diffraction

Analyses of thermal and residual microstresses between the particles and matrix of composites

Finite-element simulation of residual stress in zirconia thermal barrier coating

Real Microstructure-Based Simulation of Thermal Residual Stresses in Cemented Carbides and the Related Strengthening and Toughening Consideration

Analytical modeling of thermal residual stresses and optimal design of ZrO 2 /(ZrO 2 +Ni) sandwich ceramics

FEM analysis of internal stress of composite ceramics and its toughness mechanism

Finite Element Analysis of Stresses and Interface Crack in Tbc Systems

Mesoscopic Thermal Stress Analysis for ZrB2-SiC Ceramics