A Study of Nitrogenation of a NdFe12−xMox Compound by in Situ Neutron Powder Diffraction

CK Loong,SM Short,J Lin,Y Ding

DOI: https://doi.org/10.1063/1.367658

IF: 2.877

1998-01-01

Journal of Applied Physics

Abstract:The effects on the crystal lattice of a NdFe12−xMox (x≅1.7) during controlled nitrogenation over the 25–600 °C temperature range were studied by neutron powder diffraction. Prior to nitrogenation the sample contained a major phase of NdFe10.3Mo1.7 and a minor phase (∼12 vol %) of bcc-Fe. The sample inside the furnace was connected to a closed volume of ultrapure nitrogen gas while neutron data were collected over regular time intervals during sequential heating. Substantial nitrogen absorption occurred between 500 and 600 °C. During the nitrogenation process the NdFe12−xMoxNy lattice expanded while the bcc-Fe lattice contracted. An increasing decomposition of the compound into bcc-Fe at 600 °C was observed. The average size of the NdFe12−xMoxNy crystalline grains decreased starting at ∼300 °C, reaching a minimum at ∼500 °C and then increased markedly at higher temperatures. The development of lattice strains, on the other hand, showed an opposite trend, i.e., a maximum at 500 °C.