Effect of Nb Doping on the Microstructure and Magnetic Properties of Nd-Ce-Fe-B Alloy
Qichen Quan,Lili Zhang,Qingzheng Jiang,Weikai Lei,Qingwen Zeng,Xianjun Hu,Lei Wang,Xi Yu,Junfeng Du,Gang Fu,Renhui Liu,Minglong Zhong,Zhenchen Zhong
DOI: https://doi.org/10.1016/j.jmmm.2017.07.017
IF: 3.097
2017-01-01
Journal of Magnetism and Magnetic Materials
Abstract:With the intention to reduce the Nd content in Nd2Fe14B-type alloys, 20 at.% Ce and 0.5 at.% Nb substituting Nd and Fe in the WNd13Fe82B5 alloys were previously employed to improve successfully the coercivity and the thermal stability without the energy product reduction. In this study, a light increase of the remnant polarization J(r) was observed in (Nd0.8Ce0.2)(13)Fe-82 xNbxB5 alloy at x = 0.5 and x = 1.0, resulting from the increasing amount of alpha-Fe phase. The optimum magnetic properties obtained with 0.5 at.% Nb doping are H-cj = 13.1 kOe, J(r) = 0.79 T, (BH)(max) = 13.3 MGOe, respectively. Besides, the coercivity H-cj and maximum energy product (BH)(max) for the melt-spun ribbons with 0.5 at.% Nb addition are higher than those of the Nb-free ribbons in the temperature range of 300-450 K. Both the variations of Curie temperature T-c and a increase of lattice constants a and c of the hard magnetic phase with Nb addition imply that some of Nb atoms may directly enter into the hard magnetic phase, occupying the Fe sites. With the analysis on the demagnetization curve, Henkel curve and the observation of transmission electron microscope ( EM), the results indicate that a small amount of Nb can enhance the coercivity and exchange coupling though improving the microstructure of alloys. (C) 2017 Elsevier B.V. All rights reserved.