Theoretical calculation on the magnetocrystalline anisotropy of NdFe10.5V1.5Nx

Jinbo Yang,Bo Cui,Weihua Mao,Xiedi Pei,Yingchang Yang

DOI: https://doi.org/10.1016/S0038-1098(97)00333-5

IF: 1.934

1997-01-01

Solid State Communications

Abstract:Abstract The NdFe 10.5 V 1.5 N x compounds with different nitrogen content have been synthesized. The dependence of magnetic properties at room temperature on the nitrogen content was investigated in order to give evidence of the importance of the nitrogen content on the magnetic anisotropy of the rare earth sublattice. In the meantime, the theoretical calculations were performed to analyze the nitrogen content dependence of the magnetocrystalline anisotropy constants K 1,2 , as well as the anisotropy field H a in the NdFe 10.5 V 1.5 N x . The results confirmed that the second-order crystal-field parameter A 20 is dominant and, in the nitrides, the chief contribution to A 20 comes from nitrogen located at 2b sites. Finally, the increase of nitrogen content will first turn the easy-plane magnetocrystalline anisotropy of the rare earth sublattice into easy-axis one and then enhance it linearly to a much larger value, which is in quite good agreement with experiment.