Dielectric Study in Nanocrystalline Bi4Ti3O12 Prepared by Chemical Coprecipitation

AQ Jiang,GH Li,LD Zhang

DOI: https://doi.org/10.1063/1.367287

IF: 2.877

1998-01-01

Journal of Applied Physics

Abstract:Bi 4 Ti 3 O 12 nanoparticles were synthesized by chemical coprecipitation and crystallized in the perovskite structure after calcining at 520 °C. The dielectric properties were measured in bulk nanocrystalline compacts with different grain sizes. It was found that there were three peaks in the curves of the dielectric response as a function of temperature. The first peak shifts to higher temperature with decreasing grain size, which is considered to originate from the polarization of the ions in the conductive (Bi2O2)2+ layers across the potential barrier of the weak conductive perovskitelike layers. The second peak, contributed by the polarization of the defect dipoles on the grain surfaces, especially Bii.–Vo″ dipoles, decreases gradually in intensity and finally disappears with increasing grain size. The last one, corresponding to a ferroelectric phase transition temperature, increases at first with decreasing grain size from 56 to 25 nm, then decreases with further decreasing grain size, and the mechanism is correlated with a competing effect of the released internal stresses and the clamped domain walls due to the diffusion of oxygen vacancies.