Abstract:Single-crystal nickel-based CMSX-6 superalloy rods were directionally solidified at a constant withdrawal rate by employing a novel directional solidification process the downward directional solidification process and the Bridgman process. For the rods cast using both processes, the local cooling rates were measured at the 5.5 cm and 12.5 cm locations between the solidification front and the chill end. With an increasing distance from the chill, the cooling rate varied from 1.21 to 1.08 K/s giving a change in the rate of 10.74% in the novel process. In contrast to this, the cooling rates in the Bridgman process varied from 0.15 to 0.08 K/s giving a change in the rate of 46.67%. The microstructural evolution was comparatively investigated for the two processes as a function of the cooling rates. In comparison to the Bridgman process, refined gamma dendrite structures, smaller size of gamma/gamma' eutectic island, refined gamma' precipitates in the dendritic core and a smaller average size of microporosities were observed in both locations of the rods cast by using the novel process. In addition to this, the variations of the primary and secondary dendrite arm spacings, the size of gamma/gamma' eutectic island, and the size of gamma' precipitates in the dendrite core were smaller than those in the Bridgman process with increasing the distance from 5.5 cm to 12.5 cm. This indicates that the downward directional solidification process can cast a rod possessing more homogeneous microstructures. Moreover in comparison to the Bridgman process, the majority of the micropores have smaller diameters and both the variation in the maximum size of microporosity as well as the average diameter of these micropores located between positions near to the chill end and the distant end were smaller in the rods cast by using the novel process; the opposite is found in the Bridgman process. (C) 2014 Elsevier B.V. All rights reserved.

Solidification and microsegregation behaviors of nickel-base single crystal superalloy solidified at medium cooling rate

MICROSTRUCTURE AND MICROSEGREGATION OF Ni-BASE SINGLE CRYSTAL SUPERALLOY SOLIDIFIED AT MEDIUM COOLING RATE

Influence of Cooling Rate on the Formation of Bimodal Microstructures in Nickel-Base Superalloys During Continuous Two-Step Aging

Superfine dendrite and microsegregation of Ni-base single crystal superalloy

Solidification Behavior of Ni-based Superalloy at Different Cooling Rates

Effects of Cooling Rate on the Solidification and Microstructure of Nickel-Based Superalloy GTD222

DENDRITE REFINING AND EUTECTIC TRANSFORMATION BEHAVIOR OF NICKEL-BASE SINGLE CRYSTAL (NBSC) SUPERALLOY

Directional solidification of a Ni-based single crystal superalloy under high temperature gradient

Characterization of the Microstructure Evolution and Microsegregation in A Ni-Based Superalloy under Super-High Thermal Gradient Directional Solidification

Microstructure and Phases Structure in Nickel-Based Superalloy IN713C after Solidification

Processing, Microstructures and Mechanical Properties of a Ni-Based Single Crystal Superalloy

Microstructure and Microsegregation in A Ni-Based Single Crystal Superalloy Directionally Solidified under High Thermal Gradient

Solidification Microstructure in a Supercooled Binary Alloy

Phase Field Simulation of Alloying Element Segregation During Solidification of DD5 Nickel-Base Single Crystal Superalloy

Directional Solidification Behavior of CMSX-6 Superalloy

Microstructure and Element Segregation of Ni-Base Superalloy Casting with Radiation and Liquid-Metal Cooling

Microstructural Evolution with a Wide Range of Solidification Cooling Rates in a Ni-Based Superalloy

Microstructures and homogenization behavior of a nickel-based superalloy used for 850¬Ý‚ÑÉ turbine disc prepared by electron beam smelting layered solidification

Effect of Local Cooling Rates on the Microstructures of Single Crystal CMSX-6 Superalloy: A Comparative Assessment of the Bridgman and the Downward Directional Solidification Processes

On Morphologies, Microsegregation, and Mechanical Behavior of Directionally Solidified Cobalt-Base Superalloy at Medium Cooling Rate

Effect of Directional Solidification Variables on the Microstructures of Single-Crystal Turbine Blades of Nickel-Based Superalloy