On Morphologies, Microsegregation, and Mechanical Behavior of Directionally Solidified Cobalt-Base Superalloy at Medium Cooling Rate

Shuangjie Chu,Jianguo Li,Zhongyuan Liu,Zhengxing Shi,Hengzhi Fu

DOI: https://doi.org/10.1007/bf02651605

1994-01-01

Abstract:A newly developed experimental setup that can provide a temperature gradient of 1300 K/cm has been used in the research of the morphologies, microsegregation, and mechanical behavior of directionally solidified cobalt-base superalloy (known as K10 in PR China) at medium cooling rates from 38 to 60 K/s. Experimental results show that the primary and secondary dendrite spacings of K10 become less than one-fifth and one-eighth, respectively, of those obtainable with a conventional 100 K/cm temperature gradient and a cooling rate below 1 K/s: the carbides are directionally arrayed and the carbides’ morphology changes from islands of general cast state into worms; microsegregation is almost completely eliminated; the mechanical properties, as can be expected, are greatly superior to those obtainable with 100 K/cm temperature gradient; at 1073 K, creep-rupture strength increases from 167 to 196 MPa; endurance life is raised from 10 to 30 hours; the reduction in area increases from 12 to 52 pct; and the specific elongation increases from 17 to 46 pct. And with the increase of cooling rate, there are always corresponding improvements of mechanical properties of K10. Otherwise, the fractography of superfine columnar structure samples is high-toughness transgranular fracture, with cracks originating at the edge of carbides.